Abstract:BACKGROUND:Damaged articular cartilage has very limited capacity for spontaneous healing. Tissue engineering provides a new hope for functional cartilage repair. Creation of an appropriate cell carrier is one of the critical steps for successful tissue engineering. With the supposition that a biomimetic construct might promise to generate better effects, we developed a novel composite scaffold and investigated its potential for cartilage tissue engineering.METHODS:Chitosan of 88% deacetylation was prepared via a modified base reaction procedure. A freeze-drying process was employed to fabricate a three-dimensional composite scaffold consisting of chitosan and type II collagen. The scaffold was treated with 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide and N-hydroxysuccinimide. Ultrastructure and tensile strength of the matrix were carried out to assess its physico-chemical properties. After subcutaneous implantation in rabbits, its in vivo biocompatibility and degradability of the scaffold were determined. Its capacity to sustain chondrocyte growth and biosynthesis was evaluated through cell-scaffold co-culture in vitro.RESULTS:The fabricated composite matrix was porous and sponge-like with interconnected pores measuring from 100-250 microm in diameter. After cross-linking, the scaffold displayed enhanced tensile strength. Subcutaneous implantation results indicated the composite matrix was biocompatible and biodegradable. In intro cell-scaffold culture showed the scaffold sustained chondrocyte proliferation and differentiation, and maintained the spheric chondrocytic phenotype. As indicated by immunohistochemical staining, the chondrocytes synthesized type II collagen.CONCLUSIONS:Chitosan and type II collagen can be well blended and developed into a porous 3-D biomimetic matrix. Results of physico-chemical and biological tests suggest the composite matrix satisfies the constraints specified for a tissue-engineered construct and may be used as a chondrocyte carrier for cartilage tissue engineering.

Mechanical properties and biocompatibility characterization of 3D printed collagen type II/silk fibroin/hyaluronic acid scaffold.

Experimental Investigation and Optimal 3D Bioprinting Parameters of SA-Gel Porous Cartilage Scaffold

3D Printing of Collagen/Oligomeric Proanthocyanidin/Oxidized Hyaluronic Acid Composite Scaffolds for Articular Cartilage Repair

3D Bio-Printing of CS/Gel/HA/Gr Hybrid Osteochondral Scaffolds

Collagen-based 3D printed poly (glycerol sebacate) composite scaffold with biomimicking mechanical properties for enhanced cartilage defect repair

3D Printing Process Research and Performance Tests on Sodium Alginate-Xanthan Gum-Hydroxyapatite Hybridcartilage Regenerative Scaffolds

Development and Potential of A Biomimetic Chitosan/Type Ii Collagen Scaffold for Cartilage Tissue Engineering

Three-Dimensional Printed Silk Fibroin/Hyaluronic Acid Scaffold with Functionalized Modification Results in Excellent Mechanical Strength and Efficient Endogenous Cell Recruitment for Articular Cartilage Regeneration

3D-Bioprinted Silk Fibroin-Hydroxypropyl Cellulose Methacrylate Porous Scaffold with Optimized Performance for Repairing Articular Cartilage Defects

Development and potential of a biomimetic chitosan/type Ⅱ collagen scaffold for cartilage tissue engineering

Silk Fibroin/carboxymethyl Chitosan Hydrogel with Tunable Biomechanical Properties Has Application Potential As Cartilage Scaffold.

Designed Composites for Mimicking Compressive Mechanical Properties of Articular Cartilage Matrix

Research on Cartilage 3D Printing Technology Based on SA-GA-HA

Structurally and Functionally Optimized Silk-Fibroin-Gelatin Scaffold Using 3D Printing to Repair Cartilage Injury In Vitro and In Vivo.

3D bioprinting by reinforced bioink based on photocurable interpenetrating networks for cartilage tissue engineering

Fabrication of 3D-Printed Interpenetrating Hydrogel Scaffolds for Promoting Chondrogenic Differentiation

A 3D printed biomimetic scaffold for cartilage regeneration with lubrication, load-bearing, and adhesive fixation properties

Theoretical Prediction and Experimental Testing of Mechanical Properties for 3D Printed Silk Fibroin-Type II Collagen Scaffolds for Cartilage Regeneration

The synergistic effects of 3-D porous silk fibroin matrix scaffold properties and hydrodynamic environment in cartilage tissue regeneration

Fabrication and biocompatibility assessment of a silk fibroin scaffold with biomimetic oriented microstructure for cartilage tissue engineering

Biphasic mechanical properties of in vivo repaired cartilage