Abstract:<p>The attractive mechanical properties and superior resistance to void-swelling make ferritic/martensitic alloys a promising structural material for advanced nuclear reactors. However, one anomaly that has intrigued researchers for more than 50 years is the proportion of two types of dislocation loops in Fe and Fe-Cr alloys with Burger vectors b=½<111> and b=<100>. Although the possible mechanisms responsible for the presence of <100> loops continue to be the subject of intense modeling studies, there remains incomplete experimental understanding of fundamental irradiation processes in Fe(Cr) alloys. Here, the dose dependence of the irradiation-induced microstructural evolution was examined from 0 to 20 displacement per atom (dpa) in high purity Fe and Fe-10Cr during simultaneous dual-beam (1 MeV Kr + 10 appm He/dpa) irradiation at 435°C. We experimentally revealed that the mechanism for the formation of <100> loops may not follow the conventional simple dislocation reaction between two ½<111> loops. Real-time dynamic formation and evolution of defects including black dot loops, loop coarsening, loop decoration, network dislocations, and cavities were demonstrated. Several results indicated that the addition of Cr and He could impede dislocation loop motion. The evolution of the defect size/density and relative fraction of ½<111> vs <100> loops were quantitatively summarized. With increasing dose, ½<111> loops became the dominant type of loop in both materials. Notably, <100> loops were predominantly observed near grain boundaries only for pure Fe, while arrays of nanoscale black dot defects composing the <100> loop strings were observed in plenty in Fe-10Cr.</p>

Formation of Bubble-Loop Complexes During Helium Radiation in Fe-9Cr Steel

Effects of Temperature on Helium Bubble Behaviour in Fe–9Cr Alloy

Helium role in Fe9Cr1.5W0.4Si F/M steel during Fe++He+ dual-beam irradiation

In-situ TEM observation of microstructure evolution in Fe9Cr1.5W0.4Si alloy during He+ irradiation and post-implantation annealing

Effect of Carbon on Dislocation Loops Formation during Self-Ion Irradiation in Fe-Cr Alloys at High Temperatures

Bubble formation in helium-implanted nanostructured ferritic alloys at elevated temperatures

Dynamic observation of dual-beam irradiated Fe and Fe-10Cr alloys at 435 °C

Comparison of Helium Bubble Formation in F82H, ODS, SIMP and T91 Steels Irradiated by Fe and He Ions Simultaneously*

Dynamic behavior of helium bubbles in Fe9Cr1.5W0.4Si F/M steel at elevated temperature

An in situ study on the effect of grain boundaries on helium bubble formation in dual beam irradiated FeCrAl alloy

Dynamic evolution of polyhedral bubbles in Fe9Cr1.5W0.4Si F/M steel under 30keV H2+& He+ synergetic irradiation

Evolution mechanisms of irradiation-induced helium bubbles, C15 clusters and dislocation loops in ferrite/martensite steels: A cluster dynamics modeling study

Shrinkage and coalescence behavior of helium bubbles in Fe9Cr1.5W0.4Si F/M steel under the coupling effect of compression stress and temperature

Effect of Helium Concentration on Irradiation Damage of Fe-ion Irradiated SIMP Steel at 300 ℃ and 450 ℃

First-Principles Study of Helium Trapping in Carbide Precipitates (cr23c6) in Ferritic-Martensitic Steels

Significant suppression of helium bubbles in oxide dispersion strengthened FeCrAl alloys irradiated by high concentration of helium

Radiation Damage in Helium Ion–irradiated Reduced Activation Ferritic/martensitic Steel

Effects of minor alloying addition on He bubble formation in the irradiated FeCoNiCr-based high-entropy alloys

Radiation-Induced Helium Bubbles in Metals

Microstructure Evolution During Helium Irradiation and Post-Irradiation Annealing in a Nanostructured Reduced Activation Steel

Enhanced Helium Ion Irradiation Tolerance in a Fe-Co-Ni-Cr-Al-Ti High-Entropy Alloy with L12 Nanoparticles