Abstract:Tungsten (W) is a potential candidate for plasma facing materials (PFMs) of fusion reactor. The helium (He) produced in fusion reaction is insoluble and easy to gather and form to He bubbles in W, resulting in embrittlement and degradation of the performance of the W matrix. In this paper, based on molecular dynamics, the nucleation and growth of helium bubbles in the bulk and at ∑3[211](110) and ∑9[110](411) grain boundaries of W was studied. As a result, the growth mechanism of Helium bubbles at grain boundary of W was different from in bulk. Helium bubbles in bulk W grow up by extruding dislocation rings. The growth mechanism of helium bubbles at ∑3[211](110) grain boundary was as follows: Firstly, a small amount of W interstitial atoms were extruded and emitted. And then the 1/2 \begin{document}$\left\langle {111} \right\rangle $\end{document} dislocation line was extruded. Finally, the 1/2 \begin{document}$\left\langle {111} \right\rangle $\end{document} dislocation line would migrate along the direction of [111] of the grain boundary interface. Moreover, the emission of W interstitial atoms and dislocation extrusion of the helium bubble were not observed in our simulated time scale at the ∑9[110](411) grain boundary. Then we used the NEB method to calculate the diffusion barrier of self-gap atoms in the bulk and at ∑3[211](110) and ∑9[110](411) grain boundaries of W, which explained the simulation results. The migration energy barrier of W self-gap atoms in the bulk and at ∑3[211](110) grain boundary was only a few to a few millielectron volts. So as long as W self-gap atoms dissociated from the surface of the He bubble in the thermal relaxation process, they can be easily migrated out. However, The migration energy of the W self-gap atom at the ∑9[110](411) grain boundary can be from a few tenths to a few electron volts. Even during the thermal relaxation process, the W self-gap atoms dissociated from the surface of the He bubble. It was difficult for the W self-gap atoms migrated out. Finally, the correlation between He bubble size and stress released was given. Either in bulk or at ∑3[211](110) and ∑9[110](411) grain boundaries of W, after the pressure of the helium bubble becomes stable with time, the radius of the helium bubble would increase rapidly whenever the pressure dropped sharply. So there was a small step on the curve of the evolution of the radius of the helium bubble with time. Thus, helium bubbles in W could promote growth by releasing pressure intermittently.

Dynamic behavior of helium bubbles in Fe9Cr1.5W0.4Si F/M steel at elevated temperature

Molecular Dynamics Simulations of Helium Migration, Diffusion Behavior of Helium Bubbles, and Melting Point of Single Crystal in Bulk Γ-Fe

Shrinkage and coalescence behavior of helium bubbles in Fe9Cr1.5W0.4Si F/M steel under the coupling effect of compression stress and temperature

Dynamic evolution of polyhedral bubbles in Fe9Cr1.5W0.4Si F/M steel under 30keV H2+& He+ synergetic irradiation

Effects of Temperature on Helium Bubble Behaviour in Fe–9Cr Alloy

In-situ TEM observation of microstructure evolution in Fe9Cr1.5W0.4Si alloy during He+ irradiation and post-implantation annealing

Formation of Bubble-Loop Complexes During Helium Radiation in Fe-9Cr Steel

Bubble formation in helium-implanted nanostructured ferritic alloys at elevated temperatures

Interaction Between Recrystallization and Helium Behavior in Cold-Rolled Nickel

Helium role in Fe9Cr1.5W0.4Si F/M steel during Fe++He+ dual-beam irradiation

First-Principles Study of Helium Trapping in Carbide Precipitates (cr23c6) in Ferritic-Martensitic Steels

A multi-perspective study on the evolution behavior of helium bubbles in FeCrVTi x medium-entropy alloys

Evolution of helium bubbles induced by helium irradiation in polycrystalline palladium: An insight into tritium aging

Competitive Barrier and Trapping Effects of Helium Bubbles on Hydrogen Isotopes Migration Behavior in Tungsten

In situ TEM observation of the evolution of helium bubbles in Hastelloy N alloy during annealing

The nucleation and growth of Helium hubbles at grain boundaries of bcc tungsten: a molecular dynamics simulation

The investigation of distribution on size and concentration of helium bubbles in Y-bearing ODS steel using by SAXS and GIXRD

Modeling the helium transport and premature intergranular fracture by dislocation motion in irradiated metals

The temperature effect on the formation and growth of helium-vacancy clusters in bcc iron: a comprehensive molecular dynamics simulation

Evolution of helium bubbles in FeCoNiCr-based high-entropy alloys containing γ' nanoprecipitates

Atomistic study on helium-to-vacancy ratio of neutron irradiation induced helium bubbles during nucleation and growth in α-Fe