Abstract:The influence of chloride ion (Cl−) concentration on the corrosion mechanism of WC–MgO composites has been studied in this work. The results suggest that the corrosion resistance of WC–MgO composite decreases first and then increases with the increase in Cl− concentration. Solution conductivity and dissolved oxygen content are the main influence factors. The solution conductivity determines the charge transfer process, and the dissolved oxygen determines the cathodic oxygen absorption reaction. The corrosion characteristic is typical pitting corrosion. Meanwhile, the corrosion mechanism contains an oxidation process of the WC matrix and the dissolution destruction of the MgO toughening phase. The formation of the WO3 corrosion layer hinders the general corrosion to protect the inner material. However, the dissolution of MgO induces the initiation of pitting. The local alkaline caused by MgO dissolution promotes the dissolution of the WC matrix, which leads to the expansion of pitting.

What problem does this paper attempt to address?

The paper primarily explores the impact of chloride ion (Cl⁻) concentration on the corrosion behavior of WC–MgO composites. Specifically, the study focuses on the following aspects: 1. **Research Background**: WC–Co hard alloys are widely used in petroleum drilling and aerospace fields due to their excellent mechanical properties. However, the presence of Co binder reduces the hardness and wear resistance of the material, and with the development of the new energy industry, the demand for Co is also increasing. Therefore, researchers are striving to develop new hard materials that contain little or no Co. 2. **Research Object**: WC–MgO composites are considered potential substitutes for WC–Co hard alloys due to their low cost and easy availability, with broad application prospects. 3. **Research Purpose**: To clarify the corrosion mechanism of WC–MgO composites under different chloride ion concentrations, particularly the mechanism of pitting initiation and propagation, and the relationship between chloride ion concentration and the passivation film. 4. **Experimental Methods**: The corrosion behavior of WC–MgO composites under different chloride ion concentrations (0.1 wt.%, 1 wt.%, 3.5 wt.%, 10 wt.%) was studied through immersion tests, electrochemical tests, and microstructure analysis. 5. **Main Findings**: - With the increase in chloride ion concentration, the corrosion resistance of WC–MgO composites first decreases and then increases. - Solution conductivity and dissolved oxygen content are the main influencing factors. Solution conductivity determines the charge transfer process, while dissolved oxygen determines the cathodic oxygen absorption reaction. - The corrosion characteristics exhibit typical pitting corrosion. - The corrosion mechanism includes the oxidation process of the WC matrix and the dissolution damage of the MgO reinforcement phase. - The formed WO₃ corrosion layer hinders general corrosion, protecting the internal material; however, the dissolution of MgO initiates pitting. - The local alkalinity caused by MgO dissolution promotes the dissolution of the WC matrix, leading to the expansion of pitting. 6. **Conclusion**: The study reveals the corrosion mechanism of WC–MgO composites in neutral NaCl solution and clarifies the intrinsic factors affecting corrosion behavior under different chloride ion concentrations, providing a theoretical basis for further improving the corrosion resistance of such materials.

Influence of Chloride Ion Concentration on Corrosion Behavior of WC–MgO Composite

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Influence of concentrations of chloride ions on electrochemical corrosion behavior of titanium-zirconium-molybdenum alloy

Electrochemical corrosion behavior of hot-pressing sintered WC-Al2O3 composite in alkaline and acidic solutions

Molecular Dynamics Simulation of Reinforcing Steel Corrosion when Subjected to Both Chloride Attack and Mechanical Loading

Analysis on corrosion properties of reinforcement in concrete in chloride environment based on first-principles

Comparison on the immersion corrosion and electrochemical corrosion resistance of WC–Al 2 O 3 composites and WC–Co cemented carbide in NaCl solution

High-temperature corrosion of a Si3N4/W composite exposed to molten MgCl2-NaCl-KCl salts

Effects of W addition on the Corrosion Behaviors of FeCoNiCrMn High Entropy Alloy Composites in the 3.5 wt.% NaCl solution

Effect of Chloride Ion Concentration on Electrochemical Behavior and Corrosion Product of Am60 Magnesium Alloy in Aqueous Solutions

Attain insensitivity to chlorine ions in magnesium alloys by impeding the diffusion process

The Synergistic Inhibitions of Tungstate and Molybdate Anions on Pitting Corrosion Initiation for Q235 Carbon Steel in Chloride Solution

Studies on the Cooperative Influence of Cr and Mo on the Pitting Corrosion Resistance of Super Austenitic Stainless Steels

Sensitivity of Corrosion Behavior for Fe-Based Amorphous Coating to Temperature and Chloride Concentration

Comparison of electrochemical corrosion between coarse-grained and fine-grained WC-Al2O3 composites in acidic and alkaline solutions

Unraveling the effect of chloride ion on the corrosion product film of Cr-Ni- containing steel in tropical marine atmospheric environment

Corrosion behavior and mechanism of Cr10Mo1 steel subjected to different corrosive ions in simulated concrete pore solution

Influence of SO4 2- in aqueous solution containing Cl- on the critical pitting corrosion temperature of 316 stainless steel

Effect of Flow Rate on the Corrosion Behavior of P110 Steel in High-Ca2+ and High-Cl− Environment

Effect of ions on carbon steel corrosion in cooling systems with reclaimed wastewater as the alternative makeup water

Effects of chloride ions on corrosion of ductile iron and carbon steel in soil environments