A lithium-sulfur battery with a solution-mediated pathway operating under lean electrolyte conditions
Hui Wang,Yuyan Shao,Huilin Pan,Xuefei Feng,Ying Chen,Yi-Sheng Liu,Eric D. Walter,Mark H. Engelhard,Kee Sung Han,Tao Deng,Guoxi Ren,Dongping Lu,Xiaochuan Lu,Wu Xu,Chunsheng Wang,Jun Feng,Karl T. Mueller,Jinghua Guo,Kevin R. Zavadil,Ji-Guang Zhang
DOI: https://doi.org/10.1016/j.nanoen.2020.105041
IF: 17.6
2020-10-01
Nano Energy
Abstract:<p>Lithium-sulfur (Li–S) battery is one of the most promising candidates for the next generation energy storage systems. However, several barriers, including polysulfide shuttle effect, the slow solid-solid surface reaction pathway in the lower discharge plateau, and corrosion of Li anode still limit its practical applications, especially under the lean electrolyte condition required for high energy density. Here, we propose a solution-mediated sulfur reduction pathway to improve the capacity and reversibility of the sulfur cathode. With this method, a high coulombic efficiency (99%) and stable cycle life over 100 cycles were achieved under application-relevant conditions (S loading: 6.2 mg cm<sup>−2</sup>; electrolyte to sulfur ratio: 3 mL<sub>E</sub> g<sub>s</sub><sup>−1</sup>; sulfur weight ratio: 72 wt%). This result is enabled by a specially designed Li<sub>2</sub>S<sub>4</sub>-rich electrolyte, in which Li<sub>2</sub>S is formed through a chemical disproportionation reaction instead of electrochemical routes. A single diglyme solvent was used to obtain electrolytes with the optimum range of Li<sub>2</sub>S<sub>4</sub> concentration. Operando X-ray absorption spectroscopy confirms the solution pathway in a practical Li–S cell. This solution pathway not only introduces a new electrolyte regime for practical Li–S batteries, but also provides a new perspective for bypassing the inefficient surface pathway for other electrochemical processes.</p>
materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology