Abstract:It is known that the interest in manufacturing in a vacuum environment has increased in recent years. Thus, the wear behavior of mechanical tools under vacuum conditions has critical importance. However, adhesion and cold-welding problems between tool and working piece in vacuum conditions lead to poor wear properties and severe coefficient of friction values. Surface treatment methods such as physical vapor deposition coatings can eliminate these undesirable consequences, especially transition metal nitrides. In this study, TiAlN, TiSiN, and TiAlN/TiSiN films were coated on AISI H13 tool steels employing the cathodic arc evaporation technique. Whether the coatings grown to the substrate surface have a positive contribution to the wear performance of the substrate in the ambient air and vacuum environment was answered. Scanning electron microscope, energy dispersive spectrometer, and X-ray diffractometer analyses were used to attain structural properties. The hardness was measured using a nano-hardness tester, and the adhesion properties were determined by a scratch test. The wear behavior of the substrate and coating samples are determined under 2 N constant normal load and using WC-6%Co counter bodies under ambient air and vacuum conditions. The hardness of samples improved owing to surface coatings, and the highest nano-hardness value was determined from the TiSiN coatings as 39.42 GPa, which is ∼700% greater than the substrate. It has been observed that coated samples have superior wear performance in both wear conditions. Besides, it is determined that those tested under a vacuum condition showed superior wear resistance than the samples tested under ambient air. While TiSiN film exhibits the highest wear resistance in ambient air, the TiAlN/TiSiN layer is the best in a vacuum environment. Owing to the deposited coatings, the seizure mechanism between the friction surfaces, which is frequently encountered in the vacuum environment, is prevented, and a fascinating improvement in terms of friction coefficient is achieved.

Effects of VCN coating of PEEK gears with the PVD method on wear performance

Experimental Investigation of the Wear Behaviour of Coated Polymer Gears

Noise Evaluation of Coated Polymer Gears

Wear of AlCrN and CrAlSiN Coatings Applied to Nonstandard Involute Gears

Numerical and Experimental Investigation of the Effects of Thin Hard Coatings on the Strength of Spur Gears

Investigation of Wear, Surface, Metallurgical and Mechanical Properties of Ti6Al4V Alloys Coated with PVD Method

Effects of PVD CrAlN/(CrAlB)N/CrAlN Coating on Pin–Disc Friction Properties of Ti2AlNb Alloys Compared to WC/Co Carbide at Evaluated Temperatures

Wear behaviours of PVD-TiN coating onTi-6Al-4V alloy processed by laser powder bed fusion or conventionally processed

Wear and failure of polyoxymethylene/calcium carbonate nanocomposite gears

Study on the Tribological Behaviors of Different PEEK Composite Coatings for Use As Artificial Cervical Disk Materials

Effect of lubrication on the wear behaviour of CrN coating deposited by PVD process

Effect of Deposition Parameters on Micromechanical Properties and Machining Performance of CrN Coating for Wet Finish Turning of Ti6Al4V Alloy

An Experimental Investigation on the Wear of Lubricated Steel Against PEEK Gears

Impact-sliding wear properties of PVD CrN and WC/C coatings

Evaluation of wear mechanisms of PVD and CVD coatings deposited on cemented carbide substrates applied to hard turning

Wear studies on ZrO2-filled PEEK as coating bearing materials for artificial cervical discs of Ti6Al4V

Tribological properties of in-situ PVD TiAlN, TiSiN, and TiAlN/TiSiN coatings under ambient air and vacuum environment

Investigation of wear behavior of carbide based coated rolling roll materials under dry and lubricated conditions

Scuffing Resistance of 16MnCr5 HCR TiAlCN-Coated Gears

Comparison to Micro Wear Mechanism of PVD Chromium Coatings and Electroplated Hard Chromium

The Use of PVD Coatings for Anti-Wear Protection of the Press-In Connection Elements