Creep Behavior of a Single Crystal Nickel-Based Superalloy Containing High Concentrations of Re/Ru at an Intermediate Temperature

Ning Tian,Tai Meng,Shulei Sun,Shunke Zhang,Danping Dang

DOI: https://doi.org/10.3390/cryst14110983

IF: 2.7

2024-11-19

Crystals

Abstract:The deformation and damage mechanisms of a single crystal nickel-based superalloy containing 6.0%Re/5.0%Ru were studied through creep performance tests at 800 °C/860–880 MPa, microstructure and morphology observation, and dislocation configuration analyzation. It was found that, during the creep process at the intermediate temperature, the γ′ phase does not form a raft-like structure. After a creep fracture, the distortion degree of the cubic γ′ phase becomes greater when the observation region is closer to the fracture. The alloy has a long creep life at 800 °C, and the dislocation slipping or climbing in the γ matrix is the deformation mechanism at the early and middle creep stages. At the later creep stage, the γ′ phase is sheared by dislocations. Because of the low stacking-fault energy of the alloy, the superdislocation shearing into the γ′ phase can decompose on the {111} plane to form a (1/3) partial dislocation and stacking-fault configuration or cross-slip to the {100} plane to form the Kear–Wilsdorf (K-W) lock, which greatly improves the creep resistance of the alloy. At the later creep stage, the primary/secondary slip systems in the alloy are activated alternately, resulting in micro-cracks at the intersection of the two slip systems. As the creep progresses, the initiated cracks spread and propagate in the γ matrix phase along a direction normal to the stress axis and connect with each other until creep fracture occurs. This is the fracture mechanism of the alloy during creep at the medium temperature.

materials science, multidisciplinary,crystallography