Abstract:This study reports the formation of Er-doped nanocrystalline cobalt ferrite with the formula CoFe2-x Er x O4 (0.0 ≤ x ≤ 0.10) from nontoxic metal precursors Co(NO3)2·6H2O, Fe(NO3)3·9H2O, and Er(NO3)3·5H2O through an easy and economical sol-gel route in which citric acid is served as the chelating agent. The as-prepared powder was annealed at 700 °C for 3 h in ambient air to get the required spinel structure. The annealed samples were subjected to structural and magnetic characterization. The X-ray diffraction (XRD) data of the samples confirmed the cubic spinel structure formation. The average crystallite size evaluated from XRD data increased from 21 to 34 nm with the substitution of Er due to the larger atomic size of Er3+ than Fe3+. Moreover, the crystallite size obtained from XRD data are well matched with the particle size measured from transmission electron microscopy images. The lattice parameters obtained from XRD data agree well with the values estimated from theoretical cation distribution and Rietveld refinement calculation. The hysteresis curve exhibits the particles are soft ferromagnetic and the coercivity increased from 54.7 to 76.6 kA/m with maximum saturation magnetization, M s = 61 emug-1 for 0.10 Er content. The squareness ratios were found to be less than 0.5, which indicates the single-domain nature of our particles. The blocking temperature measured from field cooled-zero field cooled curves is T B > 350 K for all the samples, which is much higher than the room temperature (300 K). The enhancement of saturation magnetization and coercivity has been explained based on the crystallite size, anisotropy constant, and cation distribution. Thus, the structural and magnetic properties of CoFe2O4 nanoparticles (NPs) can be tuned by Er incorporation and these NPs can be applied in different soft magnetic devices.

Formation of the hard-magnetic epsilon iron oxide phase from akaganéite nanoparticles

Phase formations and magnetic properties of single crystal nickel ferrite (NiFe2O4) with different morphologies

Formation of Highly Crystalline Maghemite Nanoparticles from Ferrihydrite in the Liquid Phase

Morphologies and Magnetic Properties of α-Fe 2 O 3 Nanoparticles with Calcined at Different Temperatures

Magnetically hard ferrite nanoparticles synthesized through aerogel nanoreactor

Uncovering the Size‐Dependent Thermal Solid Transformation of Akaganéite

Sol−Gel Based Chemical Synthesis of Nd2Fe14B Hard Magnetic Nanoparticles

Competing Magnetic Interactions and Field-Induced Metamagnetic Transition in Highly Crystalline Phase-Tunable Iron Oxide Nanorods

Selective formation of iron oxide and oxyhydroxide nanoparticles at room temperature: Critical role of concentration of ferric nitrate

Preparation, phase analysis and electrochemistry of magnetite (Fe3O4) and maghemite (γ-Fe2O3) nanoparticles

Preparation and Magnetic Properties of Nanoscale Ɛ-Fe3n Particles.

Magnetic properties of co-ferrite nanoparticles prepared by co-precipitation method

Synthesis, Structure and Magnetic Properties of CoFe2O4 Ferrite Nanoparticles

Structural, Dielectric and Magnetic Studies of Cobalt Ferrite Nanoparticles for Selected Annealing Temperatures

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Fabrication of doped ferrites and exploration of their structure and magnetic behavior

Synthesis and Magnetic Properties of Cobalt Ferrite (CoFe2O4) Nanoparticles Prepared by Wet Chemical Route

Probing low temperature non-equilibrium magnetic state in Co$_{2.75}$Fe$_{0.25}$O$_{4+δ}$ spinel oxide using dc magnetization, ac susceptibility and neutron diffraction experiments

A Novel Approach to Enhance High Temperature Thermal Stability of Superparamagnetic Fe₃O₄ Nanoparticles

Synthesis of Fe2O3 nanoparticles by new Sol-Gel method and their structural and magnetic characterizations

Sol-Gel Route for the Synthesis of CoFe2- x Er x O4 Nanocrystalline Ferrites and the Investigation of Structural and Magnetic Properties for Magnetic Device Applications