Abstract:Compared with the crystalline transition metal oxyhydroxide, low-crystalline structure is conducive to high electrochemical performance due to its more grain boundaries and ion diffusion channels. However, the manufacture of low-crystalline oxyhydroxides remains challenging, especially those with multiple transition metals. Herein, high mass loading (∼9 mg cm−2) and low-crystalline Ni/Co-oxyhydroxides nanoarrays on carbon cloth (CC) were prepared by electrochemical reconstruction. The low-crystalline Ni/Co-oxyhydroxides nanoarrays possessed a hierarchical structure, which were consist of flake-like (Co0.25, Ni0.75)O(OH) single-crystals and needle-like Ni-doped CoO(OH) polycrystalline. Both single crystal nanoflakes and polycrystalline nanoneedles contained a lot of defects. Owing to the unique structure, the mutual doping of Ni and Co atoms, and the abundant defects, the nanoarrays of Ni/Co-3500 showed excellent electrochemical performance with a high specific capacitance of 8.87 F cm−2 at 5 mA cm−2 and a high rate retention of 69.33% at 50 mA cm−2, as well as a high cycle stability remaining 91.6% of initial capacitance after 2000 galvanostatic charge-discharge cycles at a current density of 20 mA cm−2. Furthermore, the assembled asymmetric supercapacitor of Ni/Co-3500//oxidized CC delivered a high areal capacitance of 1.48 F cm−2 and a volumetric capacitance of 14.8 F cm−3 at 8 mA cm−2, as well as 1.11 F cm−2 (11.1 F cm−3) even at 50 mA cm−2. The energy density of Ni/Co-3500//oxidized CC device was up to 4.35 mWh cm−3 at the powder density of 60.1 mW cm−3. It indicates that the as-prepared low-crystalline Ni/Co-oxyhydroxides arrays on CC is a promising electrode for high energy density supercapacitors.

Facile synthesis of amorphous Ni(OH) 2 nanorod array for high performance electrochromic supercapacitors

Rapid Synthesis of Mn-Doped NiFe2O4 Nanosheet Arrays for High-Performance Hybrid Supercapacitors

Hierarchical Structure Electrodes of NiO Ultrathin Nanosheets Anchored to NiCo2O4 on Carbon Cloth with Excellent Cycle Stability for Asymmetric Supercapacitors

Three-Dimensional Hierarchical Structure ZnO@C@NiO on Carbon Cloth for Asymmetric Supercapacitor with Enhanced Cycle Stability

Synthesis of amorphous Nickel-Cobalt hydroxides with high areal capacitance by one-step electrodeposition using polymeric additive

NiO hierarchical hollow nanofibers as high-performance supercapacitor electrodes

Encapsulation of Co3 O4 Nanocone Arrays via Ultrathin NiO for Superior Performance Asymmetric Supercapacitors

An electrochromic supercapacitor based on an MOF derived hierarchical-porous NiO film

New Strategy to Prepare Amorphous Nickel-Cobalt Hydroxides with High Areal Capacitance by One-Step Electrodeposition Process: Polymer As an Additive

Structure modulated amorphous/crystalline WO3 nanoporous arrays with superior electrochromic energy storage performance

Synthesis of Nickel Oxide Nanoarchitecture Crystals as an Advanced Electrode Material for Supercapacitors

Construction of hierarchical nickel cobalt sulfide@manganese oxide nanoarrays@nanosheets core‐shell electrodes for high‐performance electrochemical asymmetric supercapacitor

Controlled Growth of NiMoO4 Nanosheet and Nanorod Arrays on Various Conductive Substrates as Advanced Electrodes for Asymmetric Supercapacitors

Synchronous Defect and Interface Engineering of NiMoO4 Nanowire Arrays for High-Performance Supercapacitors

Facile growth of homogeneous Ni(OH)2 coating on carbon nanosheets for high-performance asymmetric supercapacitor applications

Facile Synthesis of Al-doped NiO Nanosheet Arrays for High-Performance Supercapacitors

Preparation of the Amorphous NiCoP Nanosheet Array on Carbon Cloth for High‐Performance Solid‐State Hybrid Supercapacitor

Low-crystalline Ni/Co-oxyhydroxides nanoarrays on carbon cloth with high mass loading and hierarchical structure as cathode for supercapacitors

Oxalate-derived porous C-doped NiO with amorphous-crystalline heterophase for supercapacitors

Construction of amorphous Ni(OH)2@nickel nanowire with interconnected structure as advanced core-shell electrodes for asymmetric supercapacitors

High-quality metal oxide core/shell nanowire arrays on conductive substrates for electrochemical energy storage.