Process and mechanism of preparing metallized blast furnace burden from metallurgical dust and sludge

Xing Gao,Yifan Chai,Yici Wang,Guoping Luo,Shengli An,Jun Peng

DOI: https://doi.org/10.1038/s41598-024-60425-8

IF: 4.6

2024-04-30

Scientific Reports

Abstract:Metallurgical dust and sludge are solid waste resources with recycling value. In recent years, rotary hearth furnace has become the most important means to treat metallurgical dust and sludge because of its wide range of raw materials and strong treatment capacity. In this study blast furnace ash and converter sludge were selected as the research objects, and high-quality metallized pellets were prepared based on the rotary hearth furnace process. The strength changed of pellets, the reduction process of iron oxides and the removal process of zinc during the roasting of pellets in rotary hearth furnace were studied. To explore the reasonable roasting condition for preparing metallized pellets in rotary hearth furnace. The optimum roasting temperature of the pellets was 1250°C and the roasting time was 25 min. The compressive strength, metallization rate and dezincification rate of metallized pellets reached 1361N, 97.44% and 95.67%, respectively. The efficient resource utilization of various metallurgical dust and sludge is realized.

multidisciplinary sciences

What problem does this paper attempt to address?

The paper mainly explores how to use the rotary kiln process to prepare high-strength, high-metallization rate, and high-dezincification rate metallized pellets from metallurgical dust. Specifically, the study selected converter sludge and blast furnace dust as research objects and prepared high-quality metallized pellets based on the rotary kiln process. The main issues the paper attempts to address are as follows:

1. **Optimization of Roasting Conditions**:
- The study investigated the effects of different roasting times and temperatures on the compressive strength, metallization rate, and dezincification rate of the pellets.
- The optimal roasting conditions were found: roasting at 1250°C for 25 minutes resulted in a pellet compressive strength of 1361N, a metallization rate of 97.44%, and a dezincification rate of 95.67%.

2. **Improving Metallurgical Performance**:
- The study explored how to improve the strength and metallization rate of the metallized pellets by optimizing the roasting conditions.
- It was found that with the extension of roasting time, the strength of the pellets first increased and then decreased; while with the increase in roasting temperature, the strength continuously increased.

3. **Dezincification Mechanism and Microstructure Changes**:
- The study examined the phase composition, microstructure, and zinc removal mechanism of the pellets under roasting conditions.
- It was confirmed that zinc mainly existed in the form of ZnO, which was reduced to zinc vapor and volatilized at high temperatures, thereby achieving efficient dezincification.

Through these studies, the paper provides theoretical guidance and technical support for the efficient comprehensive utilization of metallurgical dust.