Abstract:We report the synthesis and superconducting properties of a metastable form of the known superconductor NaxCoO2*yH2O (x ~ 1/3, y ~ 4x). Instead of using the conventional bromine-acetonitrile mixture for sodium deintercalation, we use an aqueous bromine solution. Using this method, we oxidize the sample to a point that the sodium cobaltate becomes unstable, leading to formation of other products if not controlled. This compound has the same structure as the reported superconductor, yet it exhibits a systematic variation of the superconducting transition temperature (Tc) as a function of time. Immediately after synthesis, this compound is not a superconductor, even though it contains appropriate amounts of sodium and water. The samples become superconducting with low Tc values after ~ 90 h. Tc continually increases until it reaches a maximum value (4.5 K) after about 260 h. Then Tc drops drastically, becoming non-superconducting approximately 100 h later. Corresponding time-dependent neutron powder diffraction data shows that the changes in superconductivity exhibited by the metastable cobaltate correspond to slow formation of oxygen vacancies in the CoO2 layers. In effect, the formation of these defects continually reduces the cobalt oxidation state causing the sample to evolve through its superconducting life cycle. Thus, the dome-shaped superconducting phase diagram is mapped as a function of cobalt oxidation state using a single sample. The width of this dome based on the formal oxidation state of cobalt is very narrow - approximately 0.1 valence units wide. Interestingly, the maximum Tc in NaxCoO2*yH2O occurs when the cobalt oxidation state is near 3.5. Thus, we speculate that the maximum Tc occurs near the charge ordered insulating state that correlates with the average cobalt oxidation state of 3.5.

Observation of Bulk Superconductivity in NaxCoO2.yH2O and NaxCoO2.yD2O Powder and Single Crystals

Structural and Physical Properties of the NaxCoO2·yH2O Superconducting System

Thermodynamic and Transport Measurements on Superconducting Na_xCoO_2 + yH_2O Single Crystals Prepared by Electrochemical De-intercalation

59Co, 23Na, and 1H NMR Studies of Double-Layer Hydrated Superconductors NaxCoO2-yH2O

Crystal Structure of the Sodium Cobaltate Deuterate Superconductor NaxCoO2o4xD2O (x=1/3)

23Na NMR study of non-superconducting double-layer hydrate NaxCoO2.yH2O

Superconductivity and Cobalt Oxidation State in Metastable Na(x)CoO(2-delta)*yH2O (x ~ 1/3; y ~ 4x)

Specific Heat and Superfluid Density for Possible Two Different Superconducting States in NaxCoO2·yH2O

Structural and Electronic Transport Properties of NaxCoO2

GROWTH, STRUCTURE AND PROPERTIES OF NaxCoO2 CRYSTALS

Revised superconducting phase diagram of hole doped Na$_{x}$(H$_{3}$O)$_{z}$CoO$_{2}\cdot y$H$_{2}$O

Crystal Structure and Elementary Properties of NaxCoO2 (x = 0.32, 0.5, 0.6, 0.75, and 0.92) in the Three-Layer NaCoO2 Family

Structural phase transitions and sodium ordering in Na0.5CoO2: a combined electron diffraction and Raman spectroscopy study

Thermal Expansion and Compressibility in Superconducting NaxCoO2o4xD2O (x?1/3): Evidence for Pressure-Induced Charge Redistribution

23Na NMR Studies of Non-superconducting and Superconducting Na0.35CoO2-1.3H2O (Tc < 1.8 and ~ 4.5 K)

DOPING EFFECTS IN YBa2Cu1-xCox(Cu1-yZny)2Oz SYSTEM

Enhancement of the thermopower in NaxCoO2 in the large-x regime (x⩾0.75)

Magnetic susceptibility study of hydrated and non-hydrated NaxCoO2-yH2O single crystals

Spin Correlations In Naxcoo2 With X=0.8 And 0.5

Tunneling spectroscopy of Na$_{x}$CoO$_2$ and Na$_{x}$CoO$_2$$\cdot$ yH$_2$O

Magnetic Pair-Breaking in Y1-Xhoxni2b2c (X=0, 0.25, 0.5, 0.75) Single Crystals