Abstract:As a promising energy source, direct borohydride fuel cells (DBFCs) have attracted a lot of attention. Since the electrooxidation of BH4- always accompanies the hydrolysis reaction, the energy density of DBFCs is closely related to the composition and structure of the anode. The formation of hydrogen formed by the hydrolysis of BH4- and the high exothermic nature of the reaction, as well as the strong basicity of the fuel, bring strict demands for the stability of the anode. Consequently, the designation and fabrication of an ideal anode are effective routes to enhance the performance of DBFCs. By comprehensive consideration of convenience, the electric/thermal conductivity of the electrode, the diffusion of the reactants/products and the effective cost, the electroless plating method was adopted and a CoB anode was directly formed on a Ni-foam substrate. The anode showed high electrocatalytic activities from electrooxidation of NaBH4 with a low CoB loading amount. Especially, the anode showed distinct stability compared to the CoB plate prepared by the pressed method and the catalytic activity could retain 65% after an accelerated life time test of 500 cyclic voltammetry cycles, which was due to the strong interactions between the CoB particles and Ni-foam substrate. Among all the investigated anodes, the CoB/Ni-foam electroless anode deposited for 7 times showed the best performance. It was applied in a membraneless DBFC which showed a maximum power density of 230 mW cm(-2) in 1 mol L-1 NaBH4 + 3 mol L-1 NaOH at 313 K. These characteristics allowed the electroless plating CoB/Ni-foam catalyst to exhibit enormous potential as an anode for practical applications in DBFCs.

Performance enhancement for direct borohydride fuel cells through ternary Ru–Co–B oxide catalyst

Cobalt-based N-doped Bamboo-Like Graphene Tubes with Enhanced Durability for Efficient Oxygen Reduction Reaction in Direct Borohydride Fuel Cell

Performance Degradation of A Direct Borohydride Fuel Cell

Development of the Cathode Catalyst for Direct Borohydride Fuel Cell

High Electrocatalytic Activity for Borohydride Oxidation on Palladium Nanocubes Enclosed by {200} Facets

Study of CoO as an anode catalyst for a membraneless direct borohydride fuel cell

LaNi0.9Ru0.1O3 As a Cathode Catalyst for a Direct Borohydride Fuel Cell

Boosting borohydride oxidation kinetics by manipulating hydrogen evolution and oxidation through octahedral Pt–Ni/C for high-performance direct borohydride fuel cells

The Electrocatalytic Application of RuO2 in Direct Borohydride Fuel Cells

Vacancy-assisted Oxygen Reduction Reaction on Cobalt-Based Catalysts in Direct Borohydride Fuel Cell Revealed by In-Situ XAFS and XRD

Investigation of non-precious metal cathode catalysts for direct borohydride fuel cells

Polyvinyl Alcohol Anion Exchange Resin Composite Membrane with Co@Cu Core–Shell Particles for Direct Borohydride Fuel Cell Applications

Study of the electrooxidation of borohydride on a directly formed CoB/Ni-foam electrode and its application in membraneless direct borohydride fuel cells

Development of High-Performance Cathode Catalyst of Polypyrrole Modified Carbon Supported CoOOH for Direct Borohydride Fuel Cell

Study of LaCoO3 As a Cathode Catalyst for a Membraneless Direct Borohydride Fuel Cell

A Direct Borohydride Fuel Cell Using CoPc As Cathode Catalyst

Cobalt Nickel Boride Nanocomposite As High-Performance Anode Catalyst for Direct Borohydride Fuel Cell

A Direct Borohydride Fuel Cell with a Polymer Fiber Membrane and Non-Noble Metal Catalysts.

A Direct Borohydride Fuel Cell with FeCoPc2 -Catalysed Cathode

Plasma-induced vacancy defects of Ru-doped CoFe layered double hydroxide for superior oxygen evolution activity

A cobalt-pyrrole coordination compound as high performance cathode catalyst for direct borohydride fuel cells