Role of Dibenzo Crown Additive for Improving the Stability of Inorganic Perovskite Solar Cells

Miao He,Xinyu Xu,Le Zhang,Fei Lu,Chuwu Xing,Duofa Wang,Tianjin Zhang
DOI: https://doi.org/10.3390/nano13111751
IF: 5.3
2023-05-27
Nanomaterials
Abstract:Photovoltaics are being transformed by perovskite solar cells. The power conversion efficiency of these solar cells has increased significantly, and even higher efficiencies are possible. The scientific community has gained much attention due to perovskites’ potential. Herein, the electron-only devices were prepared by spin-coating and introducing the organic molecule dibenzo-18-crown-6 (DC) to CsPbI2Br perovskite precursor solution. The current-voltage (I-V) and J-V curves were measured. The morphologies and elemental composition information of the samples were obtained by SEM, XRD, XPS, Raman, and photoluminescence (PL) spectroscopies. The distinct impact of organic DC molecules on the phase, morphology, and optical properties of perovskite films are examined and interpreted with experimental results. The efficiency of the photovoltaic device in the control group is 9.76%, and the device efficiency gradually increases with the increase of DC concentration. When the concentration is 0.3%, the device efficiency is the best, reaching 11.57%, short-circuit current is 14.01 mA/cm2, the open circuit voltage is 1.19 V, and the fill factor is 0.7. The presence of DC molecules effectively controlled the perovskite crystallization process by inhibiting the in-situ generations of impurity phases and minimizing the defect density of the film.
materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to improve the stability of inorganic perovskite solar cells. Specifically, the author improves the crystallization process of CsPbI2Br perovskite precursor solution by introducing the organic molecule dibenzo - 18 - crown - 6 (DC) as an additive, thereby enhancing the efficiency and stability of solar cells. The paper explores how DC molecules can effectively control the crystallization process of perovskite by suppressing the formation of impurity phases and reducing the film defect density, and then improve the device performance. ### Main research contents 1. **Effect of the additive**: The influence of DC molecules on the phase state, morphology and optical properties of perovskite films was studied. 2. **Experimental methods**: Perovskite films containing different concentrations of DC molecules were prepared by spin - coating method, and the films were characterized by techniques such as XRD, SEM, XPS, Raman spectroscopy and photoluminescence (PL) spectroscopy. 3. **Performance testing**: Current - voltage (I - V) and J - V curves were measured to evaluate the photoelectric performance of the device. ### Experimental results - **Crystal growth and morphology analysis**: - XRD test results show that after the introduction of DC molecules, the crystal phase of the perovskite film is not destroyed, but the diffraction peak intensity of CsBr decreases, indicating that DC molecules inhibit the formation of CsBr. - SEM images show that as the DC concentration increases, the pores on the film surface gradually decrease, and when the DC concentration is 0.3%, the film has the best morphology. - AFM measurement results show that after adding DC, the film surface becomes smoother. - **Composition and molecular interaction analysis**: - XPS analysis shows that as the DC concentration increases, the binding energy of each element shifts towards the lower energy direction, indicating that DC molecules interact with the atoms in the perovskite. - When the DC concentration is 0.3%, the XPS signal is the strongest, indicating that the device has the fewest defects at this time. - **Functional group analysis**: - FTIR spectroscopy shows that there is an interaction between DC molecules and CsI and PbI2, and the stretching vibration peak position of the C - O - C bond is shifted. - Raman spectroscopy further confirms the interaction between DC molecules and lead ions in the perovskite. ### Conclusion By introducing DC molecules, the crystallization process of perovskite can be effectively controlled, the formation of impurity phases can be inhibited, and the film defect density can be reduced, thereby significantly improving the efficiency and stability of inorganic perovskite solar cells. When the DC concentration is 0.3%, the device has the best efficiency of 11.57%, the short - circuit current is 14.01 mA/cm², the open - circuit voltage is 1.19 V, and the fill factor is 0.7.