Abstract:In order to propel the development of metal magnetic memory (MMM) technique in fatigue damage detection, the Jiles-Atherton model (J-A model) was modified to describe MMM mechanism in elastic stress stage. A series of rotating bending fatigue experiments were conducted to study the stress-magnetization relationship and verify the correctness of modified J-A model. In MMM detection, the magnetization of material irreversibly approaches to the local equilibrium state M 0 instead of global equilibrium state M an under cyclic stress, and the M 0 − σ curves are loops around the M an − σ curve. The modified J-A model is constructed by replacing M an in J-A model with M 0 , and it can describe the magnetomechanical effect well at low external magnetic field. In the rotating bending fatigue experiments, the MMM field distribution in normal direction around cylinder specimen is similar to the stress distribution, and the calculation result of model coincides with experiment result after some necessary modifications. The MMM field variation with time at a certain point in fatigue process is divided into three stages with the variation of stable stress-stain hysteresis loop, and the calculation results of model can explain not only the three stages of MMM field changes, but also the different change laws when the applied magnetic field and initial magnetic field are different. The MMM field distribution in normal direction along specimen axis reflects stress concentration effect at artificial defect, and the magnetic signal fluctuates around the defect at late fatigue stage. The calculation results coincide with the initial MMM principle and can explain signal fluctuates around the defect. The modified J-A model can explain experiment results well, and it is fit for MMM field characterization.

Theoretical and experimental analysis of the correlation between magnetic memory signals and cumulative ductile damage of butt weld under low cycle fatigue

Prediction of the Ultra-Low-Cycle Fatigue Damage of Q345qC Steel and Its Weld Joint

Study on the Prediction Method of the Ultra-Low-Cycle Fatigue Damage of Steel

Low Cycle Fatigue Properties and Fracture Mechanism of Q345qC Steel and Its Welded Joint

Fatigue Damage Analysis of Prefabricated Concrete Composite Beams Based on Metal Magnetic Memory Technique

Use of instrumented indentation testing to study local mechanical properties of 304L SS welded joints subjected to low-cycle fatigue loadings

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

Stress Evaluation of Welded Joints with Metal Magnetic Memory Testing Based on Tension–Compression Fatigue Test

A Novel Method for Characterizing the Fatigue Crack Propagation of Steel Via the Weak Magnetic Effect

Theoretical and Experimental Investigation on the Magnetomechanical Effect of Steel Bars Subjected to Cyclic Load

Characterization of Fatigue Crack Propagation of Pitting-Corroded Rebars Using Weak Magnetic Signals

Metal Magnetic Memory Inspection of Q345 Steel Specimens with Butt Weld in Tensile and Bending Test

Research on magnetic memory inspection signal characteristics of multi-parameter coupling pipeline welds

Metal Magnetic Memory Field Characterization at Early Fatigue Damage Based on Modified Jiles-Atherton Model

Effect of Tensile Stress on Self-Magnetic Leakage Field in Carbon Steel Pipe Material

Evaluation of residual load-bearing capacity for corroded steel strands via MMM technique

Quantitative Study of MMM Signal Features for Internal Weld Crack Detection in Long-Distance Oil and Gas Pipelines

A numerical simulation method of residual magnetic field signals for evaluating deformation-induced stress concentration in ferromagnetic materials

Stress State Detection Based on Metal Magnetic Memory Theory

Experimental Investigation of Fatigue Behaviour for Welded Joint with Mechanical Heterogeneity

Magnetic leakage behavior assessment in pipeline stress-concentrated areas using improved force-magnetic coupling model