Positive Magneto‐Electric Couplings in Epitaxial Multiferroic SrMnO3 Thin Film
Arup Kumar Mandal,Sourav Chowdhury,Shubham Kumar Parate,Akash Surampalli,Ritu Rawat,Kartick Biswas,Suryakanta Mondal,Pavan Nukala,D. M. Phase,R. J. Choudhary
DOI: https://doi.org/10.1002/adfm.202414855
IF: 19
2024-12-14
Advanced Functional Materials
Abstract:The study demonstrates the positive magneto‐dielectric (MD) effect of epitaxially strain multiferroic SrMnO3 thin film. Single crystalline SrMnO3 with large tetragonal distortion along with modification of crystal field (CF) induced magneto‐electric coupling. The enhancement of in‐plane Mn‐Mn bond distance is the key recipe to modify MD along with CF. This study demonstrates the magneto‐dielectric (MD) properties of high quality epitaxially strain multiferroic SrMnO3 thin film on conducting Nb doped SrTiO3 substrate. The study observes considerable high positive MD coupling near room temperature and across the anti‐ferromagnetic transition temperature of SrMnO3. The dielectric maxima of the grown film is above room temperature, which confirms the room temperature ferroelectric nature of the grown film. From out‐of‐plan polarization and PUND (Positive Up Negative Down) measurements in the presence of magnetic field, it is confirmed that the polarization value of grown SrMnO3 thin film increases with an increase in magnetic field. In this study, the oxygen off‐stoichiometry concentration is also varied by varying oxygen partial pressure during deposition and is able to create Mn4+, Mn3+, and Mn2+ in the grown films. Despite having mixed Mn states, SrMnO3 thin films remain in the insulating phase. So, the insulating nature of SrMnO3 thin film is robust with respect to oxygen off‐stoichiometry and vacancy/substrate induced strain mediated change in the crystal field. The study has also demonstrated the variation of MD in SrMnO3 thin film by change in oxygen vacancy induced modification in crystal field.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology