Enhancing powder bed fusion of alumina ceramic material: a comprehensive study from powder tailoring to mechanical performance evaluation

Mohamed Abdelmoula,Gökhan Küçüktürk,Enrique Juste,Fabrice Petit

DOI: https://doi.org/10.1007/s00170-024-13158-x

IF: 3.563

2024-02-13

The International Journal of Advanced Manufacturing Technology

Abstract:Abstract Powder bed fusion (PBF) is an additive manufacturing (AM) technique that holds a great promise for alumina ceramic materials to be processed in a one step. To ensure an effective outcome, the powder material should be thoroughly tailored, and the process parameters should be appropriately investigated. These process parameters include laser power, scanning speed, hatching space, and scanning strategies. The alumina powder has been tailored and modified to be appropriately used for PBF using the spray-drying technique, and the process parameters have been predicted and selected using a developed numerical model. Different scanning speeds of 100, 200, 300, and 400 mm/s have been considered, and the other parameters have been numerically predicted. The results demonstrated that spray drying is an effective technique for tailoring the characteristics of alumina powder, such as particle shape, particle size distribution, flowability, and absorptivity, making it ideally suited for PBF processing. Furthermore, the developed numerical model demonstrated outstanding reliability in predicting the most effective laser power and hatching space for different scanning speeds, resulting in significant cost and time savings when compared to relying solely on experimental trials. Employing a scanning speed of 400 mm/s yielded a significant improvement in relative density and quality of the printed samples surpassing other scanning speeds. Moreover, this speed effectively addressed various challenges encountered by other scanning speeds. Following the optimization of process parameters, it was determined that a relative density of 94.5% could be achieved by utilizing a scanning speed of 400 mm/s, a laser power of 210 W, and a hatching space of 30 μm. However, the evaluation of mechanical performance revealed that while the microhardness of the printed alumina samples matched the values reported in the literature, the attained compressive strength fell significantly below the values reported in the literature.

engineering, manufacturing,automation & control systems

What problem does this paper attempt to address?

The problems that this paper attempts to solve are multiple challenges encountered in the direct manufacturing of alumina ceramic materials in powder bed fusion (PBF) technology. Specifically, these challenges include:

1. **Ceramic - laser interaction**: The absorptivity of alumina to Nd - YAG or fiber lasers is very low (only 3%), which leads to insufficient energy absorption during the melting process, thus affecting the printing quality and efficiency. In order to increase the absorptivity, the researchers enhanced the absorption capacity of the powder by adding a small amount of graphite (0.1 vol%) and using spray - drying technology.

2. **Powder morphology**: The original alumina powder has a large particle size distribution (average 390.6 µm) and irregular agglomeration, which limits the fluidity and uniform distribution of the powder in the powder bed. The researchers transformed the powder into spherical particles by spray - drying technology and controlled the particle size distribution to make it more suitable for the PBF process.

3. **Process parameter optimization**: The PBF process parameters (such as laser power, scanning speed, filling spacing, layer thickness, and scanning strategy) have a significant impact on the quality of the final printed part. The researchers predicted the optimal laser power and filling spacing at different scanning speeds through numerical simulation to ensure the integrity of the melted layer and its adhesion to the lower layer, while avoiding exceeding the evaporation temperature of alumina.

4. **Mechanical property evaluation**: Although the relative density of the printed part has been increased (up to 94.5%) by optimizing the process parameters, the compressive strength of the printed sample is much lower than the values reported in the literature. This indicates that although the micro - hardness has reached the expected level, there is still room for improvement in mechanical properties.

In summary, this paper aims to improve the processing and mechanical properties of alumina ceramic materials in PBF technology through comprehensive research from powder modification to process parameter optimization.