Abstract:Temperature-programmed carburization of molybdic acid with CH4/H2 mixtures led to hexagonal Mo2C with specific surface areas ranging from 40 to 91 m2 g−1. The carburization was found to go through Mo4O11, MoO2, and Mo metal. Whatever was the parameter of carburization, no significant change of the lattice parameters of Mo2C was detected by XRD. The primary particles of the resulting carbides were found to be single crystals. Elemental analysis evidenced different bulk carbon contents of carbides depending on the conditions of synthesis. Nevertheless, this kind of analysis only gives global data to monitor the completion of carburization. Without free carbon contamination, all accessible Mo atoms were able to chemisorb oxygen. So oxygen chemisorption was proposed as a molecular probe to control the free carbon deposition. Counting of noble metal-like sites was possible by selective CO chemisorption, which was found to selectively deactivate active sites in benzene hydrogenation. CO titrated from 3 to 58% of a monolayer of surface Mo atoms. This evolution of the density of sites titrated by CO was interpreted in terms of the “degree of carburization” of materials linked to both surface carbidic carbon and residual oxygen contents as evidenced by TPR measurements of Mo2C prepared in situ. The evaluation of the quality of each Mo site titrated by CO was done by benzene hydrogenation at room temperature. The carbides were found to be as active as Ru/Al2O3. A significant increase of the activity per site was observed on Mo2C, when the density of sites titrated by CO was increased. It means that the degree of carburization affects not only the number of active sites, but also the quality of these sites. These results are in good agreement with the general concept speculated on the noble metal-like behavior of Mo2C: the higher the carbidic carbon content and the lower the residual oxygen content in Mo lattice, the higher will be the noble metal-like behavior.

Nanoscale fine-tuning of porosity of carbide-derived carbon prepared from molybdenum carbide

Highly Exposed NH2 Edge on Fragmented G‐c3n4 Framework with Integrated Molybdenum Atoms for Catalytic CO2 Cycloaddition: DFT and Techno‐Economic Assessment

Fabrication of Hierarchical Porous Carbide-Derived Carbons by Chlorination of Mesoporous Titanium Carbides

A Facile Preparation of Nanocrystalline Mo2C from Graphite or Carbon Nanotubes.

Synthesis and characterisation of porous carbide-derived carbon from SiC in Molten Salt

Atomic-Scale Mechanism on Nucleation and Growth of Mo2c Nanoparticles Revealed by in Situ Transmission Electron Microscopy

Synthesis of nanocrystalline molybdenum carbide materials and their characterization

Room Temperature Ion Beam Synthesis of Ultra-Fine Molybdenum Carbide Nanoparticles: Toward a Scalable Fabrication Route for Earth-Abundant Electrodes

Synthesis and Characterization of Molybdenum Carbide Catalysts on Different Carbon Supports

Influence of the Degree of Carburization on the Density of Sites and Hydrogenating Activity of Molybdenum Carbides

Fabrication of molybdenum carbide catalysts over multi-walled carbon nanotubes by carbothermal hydrogen reduction

Structure and Adsorption Performance of Carbide Derived Carbon

Effect of carburising agent on the structure of molybdenum carbides

Preparation of Molybdenum Carbides Using Butane and Their Catalytic Performance

Study on the Structure and Formation Mechanism of Molybdenum Carbides

Molten Alkaline Synthesis of Highly Porous Carbon from Calcium Carbide

Oxygen-Containing Functional Group-Facilitated Co2 Capture by Carbide-Derived Carbons

Silica-templated Synthesis of Ordered Mesoporous Tungsten Carbide/graphitic Carbon Composites with Nanocrystalline Walls and High Surface Areas Via a Temperature-Programmed Carburization Route.

Synthesis And Characterization Of Nanostructured Mo2c On Carbon Material By Carbothermal Hydrogen Reduction

Synthesis, structure and porosity analysis of microporous and mesoporous carbon derived from zirconium carbide

Multiscale confinement nitridation in molybdenum carbide for efficient hydrogen production