Abstract:Metal nanodendrites composed of highly branched arms have received great attention as electrocatalysts owing to their reasonably large surface area and the potential existence of low-coordinated sites in high densities. Although significant progress has been made in the synthesis of bimetallic nanodendrites, few works involve a systemconsisting of Pd and Cu, particularly in the case of alloyed nanodendrites. Here, we report a facile and powerful approach for the synthesis of PdCu alloy nanodendrites with tunable composition through varying the molar ratio of the Pd and Cu salt precursors. The key to achieving PdCu alloy nanodendrites is the use of W(CO)(6), which serves as a strong reducing agent. In addition, variation in the molar ratio of the precursors, from Pd rich to Cu rich, leads to shape evolution of the PdCu alloy, moving from a polyhedral to a dendritic nanostructure. This result indicates that galvanic replacement between a Cu rich alloy and a Pd precursor also plays an important role in the formation of PdCu alloy nanodendrites. When used as electrocatalysts for the methanol oxidation reaction (MOR), PdCu alloy nanodendrites exhibit remarkably enhanced catalytic properties relative to commercial Pd/C. Specifically, Pd35Cu65 alloy nanodendrites show the highest specific activity and mass activity for the MOR, 9.3 and 7.6 times higher than that of commercial Pd/C, respectively. This enhancement can be attributed to their dendritic structure and a possible bifunctional mechanism between Pd and Cu.

Tannic acid decorated AuPd lavender-like nanochains for enhanced oxygen reduction electrocatalysis

Au-Doped Intermetallic Pd3Pb Wavy Nanowires As Highly Efficient Electrocatalysts Toward the Oxygen Reduction Reaction

Tannic acid modified PdAu alloy nanowires as efficient oxygen reduction electrocatalysts

Facile synthesis of Rh-Pd alloy nanodendrites as highly active and durable electrocatalysts for oxygen reduction reaction.

Engineering Porosity into Trimetallic PtPdNi Nanospheres for Enhanced Electrocatalytic Oxygen Reduction Activity

Trimetallic Au@PtPd Mesoporous Nanorods As Efficient Electrocatalysts for the Oxygen Reduction Reaction

Mesoporous AgPdPt Nanotubes As Electrocatalysts for the Oxygen Reduction Reaction

PdCu Alloy Nanodendrites with Tunable Composition As Highly Active Electrocatalysts for Methanol Oxidation

Intermetallic Pd3Pb Ultrathin Nanoplate-Constructed Flowers with Low-Coordinated Edge Sites Boost Oxygen Reduction Performance

Facile Synthesis of Porous Dendritic Bimetallic Platinum-Nickel Nanocrystals As Efficient Catalysts for the Oxygen Reduction Reaction

Ultrafine PdAgAu alloy nanowires for ethanol oxidation electrocatalysis

Trimetallic Au@PdPt porous core-shell structured nanowires for oxygen reduction electrocatalysis

Porous PdAg alloy nanostructures with a concave surface for efficient electrocatalytic methanol oxidation

Defect-rich ultrathin AuPd nanowires with Boerdijk–Coxeter structure for oxygen reduction electrocatalysis

Aqueous Synthesis of Au10Pt1 Nanorods Decorated with MnO2 Nanosheets for the Enhanced Electrocatalytic Oxidation of Methanol

Pt-Decorated PdCo@Pd/C Core-Shell Nanoparticles with Enhanced Stability and Electrocatalytic Activity for Oxygen Reduction Reaction

Hierarchical defective palladium-silver alloy nanosheets for ethanol electrooxidation

Strain-Modulated Platinum-Palladium Nanowires for Oxygen Reduction Reaction.

Facile synthesis of trimetallic AuPtPd alloy nanowires and their catalysis for ethanol electrooxidation

Direct epitaxial growth of Au nanoparticles on Pd metallene enables robust oxygen reduction electrocatalysis

Five-fold twinned Pd2NiAg nanocrystals with increased surface Ni site availability to improve oxygen reduction activity.