Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Iron nanoparticle formation in a metal-organic matrix: from ripening to gluttony

Synthesis of iron–nickel nanoparticles via a nonaqueous organometallic route

Mechanistic Insights into Nanoparticle Formation from Bimetallic Metal–Organic Frameworks

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Multilayer Route to Iron Nanoparticle Formation in an Insulating Matrix

Time-resolved in situ studies on the formation mechanism of iron oxide nanoparticles using combined fast-XANES and SAXS

Formation of Iron (Hydr)Oxide Nanoparticles with a pH-Clock

Exploring the fabrication and transfer mechanism of metallic nanostructures on carbon nanomembranes via focused electron beam induced processing

Controlling Nanoparticle Synthesis Derived from Bimetallic Metal–organic Frameworks

Direct observation of the formation and stabilization of metallic nanoparticles on carbon supports

Aerosol synthesis of phase-controlled iron-graphene nanohybrids through FeOOH nanorod intermediates.

Synthesis of Nearly Monodisperse Iron Oxide and Oxyhydroxide Nanocrystals

Controlled Synthesis of Magnetic Iron Oxide Nanoparticles: Magnetite or Maghemite?

Transition Metal (Fe, Co, Ni) Oxide Micro/Nanostructures: Phase, Morphology, and Decomposition of Precursors

Discovery of molecular intermediates and non-classical nanoparticle formation mechanisms by liquid phase electron microscopy and reaction throughput analysis

Synthesis of iron oxide nanorods via chemical scavenging and phase transformations of intermediates at ambient conditions

Iron-based trinuclear metal-organic nanostructures on a surface with local charge accumulation

Microwave-assisted Flow Synthesis of Multicore Iron Oxide Nanoparticles

Fe3-Xtixo4 Nanoparticles As Tunable Probes Of Microbial Metal Oxidation

Watching metal nanoparticle exsolution

Characterization of Fe Nanorods Grown Directly from Submicron-Sized Iron Grains by Thermal Evaporation