Abstract:The local environment of manganese atoms in LaMnO3 under pressure up to 15.3 GPa has been studied by x-ray absorption spectroscopy. For pressures below 8 GPa, no change is detected within the MnO6 octahedra. Above this pressure a continuous reduction of the long Mn-O distance takes place, however the octahedral distortion persists over the whole pressure range. At 15.3 GPa the average Jahn-Teller splitting of the distances is reduced by about one third, indicating that a total removal of the local Jahn-Teller distortion would occur only for pressures around 30 GPa, where metallization is reported to take place. A hysteresis in the long distance reduction is observed down to ambient pressure, suggesting the coexistence of MnO6 distorted and undistorted units.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: How does the local environment of manganese atoms in LaMnO₃ (especially the distortion caused by the Jahn - Teller effect) change under high - pressure conditions. Specifically, the researchers hope to explore the local structural changes of LaMnO₃ under different pressures through X - ray absorption spectroscopy (XAS) technology, especially the relationship between the Jahn - Teller distortion and the insulator - metal transition. ### Main problems: 1. **Stability of Jahn - Teller distortion**: The MnO₆ octahedron in LaMnO₃ is distorted due to the Jahn - Teller effect, forming 4 short bonds and 2 long bonds. The researchers hope to understand the stability of this distortion under high - pressure conditions. 2. **Effect of high pressure on local structure**: Through X - ray absorption spectroscopy, the researchers hope to reveal the specific effect of high pressure on the local structure of the MnO₆ octahedron, especially the changes in long and short bonds. 3. **Relationship between Jahn - Teller distortion and insulator - metal transition**: LaMnO₃ undergoes an insulator - metal transition under high pressure, and the researchers hope to explore through experimental data whether this transition is related to the disappearance of the Jahn - Teller distortion. ### Research background: LaMnO₃ is a material with complex physical properties, especially showing antiferromagnetic semiconductor behavior in its ground state, and having an orthorhombic - distorted cubic perovskite lattice structure. The Jahn - Teller effect of Mn³⁺ ions causes the MnO₆ octahedron to be distorted, forming 4 short bonds and 2 long bonds. Previous studies have shown that high pressure can reduce lattice distortion and enhance carrier mobility, but the specific local structural changes have not been fully understood. ### Research methods: The authors used X - ray absorption spectroscopy (XAS) technology, especially near - edge X - ray absorption fine structure (XANES) and extended X - ray absorption fine structure (EXAFS), to study the local structural changes of LaMnO₃ in the range of 0 to 15.3 GPa. In the experiment, a diamond anvil cell device with perforations was used to overcome the difficulties in collecting XAS data under high - pressure conditions. ### Key findings: - Below 8 GPa, there is no obvious change in the local structure of the MnO₆ octahedron. - Above 8 GPa, the long bonds (Mn - O) gradually shorten, but the Jahn - Teller distortion still exists. - At 15.3 GPa, the Jahn - Teller splitting distance is reduced by about one - third, and it is speculated that the Jahn - Teller distortion will completely disappear at around 30 GPa. - When the pressure is released, a hysteresis phenomenon is observed, indicating that there may be coexistence of distorted and undistorted MnO₆ units. ### Conclusion: The research shows that the Jahn - Teller distortion in LaMnO₃ gradually weakens under high pressure, but will not completely disappear before 30 GPa. This implies that there is a close relationship between the Jahn - Teller distortion and the insulator - metal transition. In addition, the existence of the hysteresis phenomenon indicates that there may be coexistence of distorted and undistorted MnO₆ units under high pressure.

Stability of Jahn Teller distortion in LaMnO3 under pressure: An x-ray absorption study

Effects of Pressure on Electron Transport and Local Structure of Manganites: Low to High Pressure Regime

High pressure behavior of Ga-doped LaMnO_3: a combined X-ray diffraction and optical spectroscopy study

Structural Transition of Mnnb2o6 under Quasi-Hydrostatic Pressure

The Structural Stability of Mn3Sn Heusler Compound under High Pressure.

High Pressure Structural Stability of Multiferroic Hexagonal REMnO3

Structural stability and electrical properties of AlB2-type MnB2 under high pressure

Pressure-Induced Magnetic Transition In Manganite (La0.75ca0.25mno3)

Strain induced stabilization of a static Jahn-Teller distortion in the O$^*$-phase of La$_{7/8}$Sr$_{1/8}$MnO$_3$

Pressure-Induced Structural Distortion of Tbmno3: A Combined X-Ray Diffraction and X-Ray Absorption Spectroscopy Study

Compressibility of natural manganite at high pressure: Influence of Jahn-Teller effect and hydrogen bond

High-Pressure Structural Stability of Multiferroic Hexagonal Rmno3 (R = Y, Ho, Lu)

Pressure dependence of phase transition in undoped LaMnO3

Pressure effects on the magnetic structure in La0.5Ca0.5-xSrxMnO3 (0.1 -< x -< 0.4) manganites

Pressure-dependent electronic structures and orbital hybridization of Mn 3 d states in multiferroic BiMnO 3 : A combined x-ray absorption, x-ray emission, and resonant x-ray emission study

High‐pressure studies of Mn2(C2H6N6)4(NO3)4·2H2O by Raman scattering, infrared absorption, and synchrotron X‐ray diffraction

Phase Transition and Vibration Properties of MnCO3 at High Pressure and High-Temperature by Raman Spectroscopy

High-pressure effects on structural, magnetic, and vibrational properties of van der Waals antiferromagnet

Modifications of Mno6 Octahedra in Dymno3 under High Pressure

Structure searching and phase relations in MnN up to 50 GPa: a DFT study