Structural Transition of Mnnb2o6 under Quasi-Hydrostatic Pressure

Fengxian Huang,Qiang Zhou,Liang Li,Xiaoli Huang,Dapeng Xu,Fangfei Li,Tian Cui

DOI: https://doi.org/10.1021/jp503542y

2014-01-01

Abstract:High-pressure Raman scattering and X-ray diffraction studies on manganese niobate (MnNb2O6) have been carried out in a diamond anvil cell at room temperature up to 41 GPa. A pressure-induced phase transition was observed at 12 GPa accompanied by the softening of two internal vibration modes v(10)(B-2g) and v(8)(A(g)). Disappearing of most Raman vibration peaks under high pressure reveals that the NbO6 octahedra distort heavily through the transition; this is evidenced by the X-ray diffraction results, but the octahedral units still exist, as the internal Nb-O strengthening vibration is observable even at the highest pressure in this study. The equation of state for MnNb2O6 in low pressure phase I was obtained with third-order Birch-Murnaghan method, yielding a zero-pressure bulk modulus B-0 and its pressure derivative B-0' of 154.4 +/- 3.5 GPa and 4.1, respectively. The volume dependencies of the optical lattice mode frequencies and their respective Griineisen parameters were extracted; it is suggested that the instability of the columbite orthorhombic structure at high pressure is related to the strong deformation of the NbO6 octahedra. Decompression measurements suggest that the pressure-induced transformation is partly reversible.