Abstract:Monocore powder-in-tube MgB2 strands were cold-drawn and heat-treated at 600C and 700C for times of up to 71 hours and structure-property relationships examined. Drawing-induced elongation of the Mg particles led, after HT, to a textured macrostructure consisting of elongated polycrystalline MgB2 fibers separated by elongated pores. The superconducting Tc, Jc and Fp were correlated with the macrostructure and grain size. Grain size increased with HT time at both 600C and 700C. Jc and hence Fp decreased monotonically but not linearly with grain size. Overall, it was observed that at 700C, the MgB2 reaction was more or less complete after as little as 30 min; at 600C, full reaction completion did not occur until 71 h. into the HT. Transport, Jct(B) was measured in a perpendicular applied field, and the magnetic critical current densities, Jcm\bot(B) and Jcm{\phi}(B), were measured in perpendicular and parallel (axial) applied fields, respectively. Particularly noticeable was the premature dropoff of Jcm\bot(B) at fields well below the irreversibility field of Jct(B). This effect is attributed to the fibrous macrostructure and its accompanying anisotropic connectivity. Magnetic measurements with the field directed along the strand axis yielded a critical density, Jcm\bot(B), for current flowing transversely to the strand axis that was less than and dropped off more rapidly than Jct(B). In the conventional magnetic measurement, the loop currents that support the magnetization are restricted by the lower of Jct(B) and Jcm{\phi} (B). In the present case the latter, leading to the premature dropoff of the measured Jcm(B) compared to Jct(B) with increasing field. This result is supported by Kramer plots of the Jcm{\phi} (B) and Jct(B) data which lead to an irreversibility field for transverse current that is very much less than the usual transport-measured longitudinal one, Birr,t.

Magnetic shielding properties of high-temperature superconducting tubes subjected to axial fields

Investigation on intense axial magnetic field shielding with a large melt cast processed Bi-2212 tube

Behavior of bulk high-temperature superconductors of finite thickness subjected to crossed magnetic fields

Magneto-thermal phenomena in bulk high temperature superconductors subjected to applied AC magnetic fields

Resistive upper critical magnetic field of a superconducting Bi-2201 thin film grown on a vicinal substrate

Upper Critical Fields Well above 100 T for the Superconductorsmfeaso0.85f0.15withtc

Simulation of Ferromagnetic Shielding to the Critical Current of Bi2223/Ag Tape under External Fields

Shielding superconductors with thin films

Gamma radiation effects on high-temperature superconducting ReBCO tape

Superconducting Transition Width under Magnetic Field in Mgb2 Polycrystalline Samples

Drawing induced texture and the evolution of superconductive properties with heat treatment time in powder-in-tube in-situ processed MgB2 strands

HPCVD Thin Film MgB2 for Superconducting Magnetic Shielding

Finite Element Models for Magnetic Shields Made of Stacked Superconducting Tape Annuli

AC Magnetic Susceptibility: Mathematical Modeling and Experimental Realization on Poly-Crystalline and Single-Crystalline High-Tc Superconductors YBa2Cu3O7−δ and Bi2−xPbxSr2Ca2Cu3O10+y

Magnetic Shielding Capability of MgB2 Cup Made by Liquid Infiltration Process

Improving the screening ability of high-temperature superconductors by combining disk-shaped bulks and closed-loop coated conductors

A pulsed current set-up for use in magnetic fields above 30 T; application to high-temperature superconductors

Uniaxial Linear Resistivity of Superconducting La1.905ba0.095cuo4 Induced by an External Magnetic Field

Angular dependence of direct current decay in a closed YBCO double-pancake coil under external AC magnetic field and reduction by magnetic shielding

The Effect of Magnetic Fields, Temperature and Current on the Resistivity of Bi-2223 High Temperature Superconductors