Abstract:In addition to activity, durability of Pd-based catalysts in a highly corrosive medium has become one of the most important barriers to limit their industrial applications such as low-temperature fuel cell technologies. Here, Rh with a unique capability to resist against oxidation etching was incorporated into Pd-based catalysts to enhance both their activity and durability for oxygen reduction reaction (ORR). This idea was achieved through the synthesis of the Rh-Pd alloy nanodendrites by co-reducing Rh and Pd salt precursors in oleylamine (OAm) containing cetyltrimethylammonium bromide (CTAB). In this synthesis, Rh-Pd alloy nanostructures with Rh-Pd atomic ratios from 19 : 1 to 1 : 4 were generated by varying the molar ratios of Rh and Pd salt precursors. Interestingly, this variation of the molar ratios of the precursors from Rh rich to Pd rich would lead to the shape evolution of Rh-Pd alloy from dendritic nanostructures to spherical aggregations. We found that Br- ions derived from CTAB were also indispensible to the production of Rh-Pd alloy nanodendrites. Owing to the addition of highly stable Rh as well as the radical structure with a large number of low-coordinated sites on the arms, Rh-Pd alloy nanodendrites with a Rh-Pd atomic ratio of 4 : 1 (Rh80Pd20) exhibited a substantially enhanced electrocatalytic performance towards ORR with a 5% loss of mass activity during the accelerated stability test for 10 000 cycles compared to similar to 50% loss of the commercial Pt/C (E-TEK).

Phosphorus modulation of a mesoporous rhodium film for enhanced nitrogen electroreduction

Modulation of surface properties on cobalt phosphide for high-performance ambient ammonia electrosynthesis

Boosting the Activity of Fe-Nx Moieties in Fe-N-C Electrocatalysts Via Phosphorus Doping for Oxygen Reduction Reaction

Boosting Electrochemical Nitrogen Fixation by Mesoporous Rh Film with Boron and Sulfur Co-Doping

Bimetallic mesoporous RhRu film for electrocatalytic nitrogen reduction to ammonia

Facile synthesis of Rh-Pd alloy nanodendrites as highly active and durable electrocatalysts for oxygen reduction reaction.

Near‐ and long‐range electronic modulation of single metal sites to boost CO2 electrocatalytic reduction

Phosphorus and Nitrogen Dual Doped and Simultaneously Reduced Graphene Oxide with High Surface Area As Efficient Metal-Free Electrocatalyst for Oxygen Reduction

Electronegative Phosphorus-Integrated Co 2+ Active Sites for Enhanced Electrocatalytic Nitrogen Reduction

Interstitial Boron-Doped Nanoporous Palladium Film for Electro-Reduction of Nitrogen to Ammonia

Surface engineering of Rh-modified Pd nanocrystals by colloidal underpotential deposition for electrocatalytic methanol oxidation

Phosphorus modification of cobalt–iron nanoparticles embedded in a nitrogen-doped carbon network for oxygen reduction reaction

Phosphorus incorporation accelerates ammonia electrosynthesis over mesoporous Au film

Regulating the frontier orbital of iron phthalocyanine with nitrogen doped carbon nanosheets for improving oxygen reduction activity

Modulating surface electronic structure of mesoporous Rh nanoparticles by Se-doping for enhanced electrochemical ammonia synthesis

Metal–metalloid alloys: mesoporous Rh–Te films for electrocatalytic nitrogen fixation

Surface hydrophobic modification enhanced catalytic performance of electrochemical nitrogen reduction reaction

Ionic-liquid-induced phthalocyanine monolayer electrocatalyst for efficient nitrogen reduction reaction

Phosphorus-bridged ternary metal alloy encapsulated in few-layered nitrogen-doped graphene for highly efficient electrocatalytic hydrogen evolution

High-Performance Rh2P Electrocatalyst for Efficient Water Splitting.

Transition metal and phosphorus co-doping induced lattice strain in mesoporous Rh-based nanospheres for pH-universal hydrogen evolution electrocatalysis