Multifunctional Electromagnetic Interference Shielding Ternary Alloy (Ni–W–P) Decorated Fabric with Wide-Operating-Range Joule Heating Performances

Yu Bai,Feng Qin,Yinxiang Lu
DOI: https://doi.org/10.1021/acsami.0c15134
2020-10-12
Abstract:Flexible electromagnetic interference (EMI) shielding textiles with wide-operating-range Joule heating performances are urgently indispensable in the application of artificial intelligence, communication industry, and wearable electronics. Herein, a simple and cost-effective approach is proposed to construct multifunctional textiles by electroless depositing a nickel–tungsten–phosphorus (Ni–W–P) ternary alloy on a polyamide (PA) fabric. The resultant fabric with a thickness of ∼117 μm exhibits a favorable EMI shielding effectiveness (SE) of 43.6 dB within 2–12.5 GHz. Particularly, finite difference time domain (FDTD) simulation was introduced to investigate the effects of the PA fabric mesh number and Ni–W ratio on the EMI SE value, which was validated by experimental results. In addition, the conductive fabric demonstrates excellent heating efficiency (up to 140 °C under 2 V within 60 s), a wide operating range (from 40 to 140 °C), and simultaneously, satisfactory reproducibility by undergoing dozens of heating and cooling cycles. Notably, EMI SE of the multifunctional fabric remains unchanged even after a series of durability measurements including 180 °C heating, ultrasonication treatment, and repetitive peeling tests, respectively. Therefore, the prepared Ni–W–P coated PA fabric with prominent chemical stability and mechanical robustness endows enormous potential in multi-scene applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c15134?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c15134</a>.Electroless nickel plating laboratory process; parameters employed in simulation of the Ni–W–P-N3 coated PA-5 fabric; experimental platform for high-temperature resistance measurement; EDX analysis and elemental composition for the Ni–W–P-N3 coated PA-5 fabric; FTIR spectra of the PA fabric and PA-NH<sub>2</sub> fabric; XPS spectra of W 4f, P 2p, and P loss; XPS spectra of N 1s from the PA-NH<sub>2</sub> fabric and Ni–W–P-N3 coated PA-5 fabric; digital image of the Ni–W–P-N3 coated PA-3 fabric and the unit for Ni–W–P-N3 coated PA-3 fabric; magnetic hysteresis loops for the Ni–W–P-N3 coated PA-3 fabric sample; two-dimensional electric field intensity distribution profiles; EMI SEs of the Ni–W–P-N<i>x</i> coated PA-5 fabric at frequencies of 4 and 10 GHz; digital photograph of the real-time monitoring platform; digital diagrams of the three fabrics at different temperatures; schematic image of the Scotch tape test for the ternary alloy coated flexible conductive fabric; XPS atomic ratio (%) of fabric samples; corrosion current density (<i>I</i><sub>corr</sub>) and corrosion recording potential (<i>E</i><sub>corr</sub>) of the Ni–W–P-N3 coated PA-5 fabric and single metal Ni coated fabric (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c15134/suppl_file/am0c15134_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology
What problem does this paper attempt to address?