Impact of chain fragmentation on charge transfer scenario and two-plateaus-like behavior of Tc(x) in YBa2Cu3O6+x

V. M. Matic,N. Dj. Lazarov

DOI: https://doi.org/10.1016/j.ssc.2007.01.041

2006-11-09

Abstract:A model of charge transfer mechanism from CuO chains to CuO2 planes has been proposed to account for doping of the planes, assuming that only chains containing more than three oxygen atoms can contribute to hole transfer. Only chains with length l greater than 4 are assumed to have transferred a certain fraction, approximately 40%, of the holes created by oxygen atoms added to the chain beyond the first three oxygen atoms. Using the so obtained x dependence of doping, p(x), at constant (room) temperature and utilizing empirical parabolic phase relation Tc(p) (Tc(p)=Tc,max[1-82.6(p(x)-0.16)2], the Tc versus x dependence is obtained to have two clearly distinguished plateaus at 60K and 90K, remarkably fitting to experimental Tc(x). The effect of statistics of CuO chain fragmentation has been included by applying cluster variation method to two dimensional asymmetric next nearest neighbor Ising model that is employed to describe oxygen-chain ordering in basal planes. The obtained results indicate that plateaus, coinciding with dTc(x)/dx=0, emerge either when dp(x)/dx=0 (p(x)=const), in the region of OII phase formation (the 60K plateau), or when p=0.16, representing the optimal doping at x=0.91 in OI phase (the 90K plateau).

Superconductivity,Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explain how the breakage of oxygen chains in YBa₂Cu₃O₆₊ₓ (yttrium barium copper oxide) superconductors affects the charge - transfer mechanism and leads to the appearance of two distinct plateaus (60K and 90K) in the critical temperature \(T_c(x)\). Specifically, the researchers focused on the following points:

1. **Charge - transfer mechanism**: A model of charge transfer from CuO chains to CuO₂ planes was proposed, assuming that only chains longer than three oxygen atoms can contribute to hole transfer. In particular, only chains with length \(l\geq4\) can transfer approximately 40% of the holes.

2. **Two - plateau behavior**: By introducing the critical chain length \(l_{cr}\), the researchers attempted to explain why \(T_c(x)\) exhibits two distinct plateaus at different doping concentrations \(x\). These two plateaus appear at 60K and 90K respectively, which are highly consistent with the experimental results.

3. **Statistical effects**: The statistical effects of CuO chain breakage were considered, and the Cluster Variation Method (CVM) combined with the two - dimensional asymmetric next - nearest - neighbor Ising model (ASYNNNI model) was applied to describe the arrangement of oxygen chains in the basal plane.

### Specific problems

- **Influence of critical chain length**: The researchers explored the influence of different critical chain lengths \(l_{cr}\) on the shape of the \(T_c(x)\) curve. When \(l_{cr} = 4\), the calculation results are most consistent with the experimental data.

- **Optimal doping level**: The optimal doping level \(p = 0.16\) holes/copper site, corresponding to the 90K plateau at \(x\approx0.91\), was analyzed.

- **Phase - change behavior**: The influence of the formation of the OII phase on the 60K plateau and the role of the OI phase at higher oxygen contents were studied.

### Main conclusions

- **60K plateau**: Related to the formation of the OII phase, manifested as doping level \(p(x)\approx\text{const}\).

- **90K plateau**: Corresponds to the optimal doping level \(p = 0.16\), reaching the maximum \(T_c\) at \(x\approx0.91\).

Through these analyses, the researchers not only explained the two - plateau phenomenon of \(T_c(x)\), but also revealed the intrinsic connection between the oxygen chain length distribution and the charge - transfer mechanism.