Delignified wood/polyethylene glycol-based material with BN as thermal conductive filler for thermal energy storage

Yanchen Li,Junqi Zhao,Xiaoyang Fang,Jingmeng Sun,Shumin Chen,Weiye Zhang,Beibei Wang,Daihui Zhang,Yi Liu,Hongwu Guo

DOI: https://doi.org/10.1016/j.est.2023.107835

IF: 9.4

2023-06-03

Journal of Energy Storage

Abstract:In this work, phase change energy storage wood () was obtained by injecting PGMA into the porous tissue of wood by high temperature and high pressure method, and the BN grafted with KH550 and DA (KH550-DA-BN) was synthesized to improve the heat transfer rate. Studies have found that PGMA has good thermal conductivity in the cavities of woody cells. After adding KH550-DA-BN to PGMA, the KH550-DA-BN combines with PGMA in a physically dispersed manner and the crystal structure of PGMA does not change. When the filling amount of KH550-DA-BN is 6 wt%, the thermal conductivity of increases to 0.4185 W/(m·K), its melting enthalpy and solidification enthalpy are all maintained at 103.40 J/g and 100.20 J/g, respectively. The shows efficient solar-to-thermal energy conversion and a lasting heat storage capacity under simulated sunlight. After 200 cycles of cooling and heating, the melting enthalpy and solidification enthalpy of are both above 120 J/g, indicating that has good stability in use. There is no leakage of 6 % after heated at 80 °C for 4 h, due to the interpenetrating network structure between PGMA and wood components. The phase change heat storage wood prepared in this research increases the potential of wood for temperature regulation in fields such as building materials, furniture and aerospace.

energy & fuels