Fretting wear resistance at ambient and elevated temperatures of 316 stainless steel improved by laser cladding with Co-based alloy/WC/CaF 2 composite coating

Haitao Ding,Yue Cao,Ke Hua,Yanlin Tong,Na Li,Linghong Sun,Xiaolin Li,Hongxing Wu,Haifeng Wang

DOI: https://doi.org/10.1016/j.optlastec.2023.109428

2023-04-07

Abstract:The coating fabricated by laser cladding on the surface has been an effective way to strengthen and enhance the wear resistance of alloys. However, the traditional Co-based alloy coatings rarely pay attention to the addition of self-lubrication constituents to form the composite coating. In addition, the effects of the Co-based composite coating on fretting wear resistance were few addressed. In this study, a Co-based alloy/WC/CaF 2 composite coating was fabricated by laser cladding on the surface of 316 stainless steel to improve the surface hardness and self-lubrication performance. The microstructure, phase constituents and fretting wear resistance at both room temperature (RT) and 500 °C were investigated. Results confirm that the composite coating is consisting of α-Co, Cr 23 C 6 and WC phases. And the F element is effectively dissolved into the α-Co phase. The fabricated composite coating is dense and uniform. The microhardness of the composite coating can reach to 600 HV 0.2 due to the presence of WC and Cr 23 C 6 phase. In addition, the grain refinement is another reason resulting in the higher microhardness. Fretting tests demonstrate that the fretting wear resistance at both RT and 500 °C are significantly improved by the composite coating, which can lead to the decrease of the COF and the wear loss. The lower COF can be ascribed to the dissolved F element in α-Co phase, especially at high fretting temperature. Additionally, the composite coating can effectively prevent the oxidation during fretting both at RT and 500 °C. This work provides an excellent method for the metallic materials to improve fretting wear resistance at both RT and high temperature.

optics,physics, applied