Bi 2 O 3 Induced Ultralong Cycle Lifespan and High Capacity of MnO 2 Nanotube Cathodes in Aqueous Zinc-Ion Batteries
Lei Gou,Shao-Pan Zhao,Wen-Qi Wang,Lei Xu,Wen-Yan Wang,Jun Wu,Zhe-Fan Ma,Xiaoyong Fan,Dong-Lin Li
DOI: https://doi.org/10.1021/acsaem.1c01495
IF: 6.4
2021-07-14
ACS Applied Energy Materials
Abstract:MnO<sub>2</sub> is regarded as a promising cathode for aqueous rechargeable zinc-ion batteries (ARZBs) due to its high theoretical capacity and high voltage. However, it still faces unsatisfied long-term cycling durability due to the John–Teller effect and the formation of the irreversible phase during cycling. Herein, this issue is addressed by constructing a hybrid cathode with a facile commercial strategy involving a uniform mixture of Bi<sub>2</sub>O<sub>3</sub> and MnO<sub>2</sub> nanotubes. The multiple effects of adding Bi<sub>2</sub>O<sub>3</sub> are deeply revealed by means of the electrochemical kinetics test, charge–discharge mechanism investigation, phase and structural evolution analyses, as well as density functional theory (DFT) calculations. It is found that the in situ-formed Bi<sup>3+</sup> can not only enhance the structural stability and alleviate the dissolution of Mn<sup>3+</sup> by forming Mn–O bonds with MnO<sub>2</sub>, but also lead to better transport kinetics of Zn<sup>2+</sup> by the competitive formation of Bi<sub>2</sub>Mn<sub>4</sub>O<sub>10</sub> that can inhibit the irreversible ZnMn<sub>2</sub>O<sub>4</sub> produced during the repeated H<sup>+</sup> and Zn<sup>2+</sup> coinsertion/extraction process. Moreover, the tunnel-like Bi<sub>2</sub>Mn<sub>4</sub>O<sub>10</sub> can contribute an additional capacity by the insertion of H<sup>+</sup>. Benefiting from these, the MnO<sub>2</sub>/Bi<sub>2</sub>O<sub>3</sub> hybrid cathode delivers high capacities of 120 and 80 mAh g<sup>–1</sup> even after 5000 cycles at the current densities of 3000 and 10 000 mA g<sup>–1</sup>, respectively. This design provides an effective and scalable pathway to enhance the electrochemical performance of the MnO<sub>2</sub> cathode and may speed up the commercial application of ARZBs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c01495?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c01495</a>.Long-term cycling performances of MnO<sub>2</sub>-Bi<sub>2</sub>O<sub>3</sub>-5, MnO<sub>2</sub>-Bi<sub>2</sub>O<sub>3</sub>-15, and MnO<sub>2</sub>-Bi<sub>2</sub>O<sub>3</sub>-20 and the cycling performance of the Bi<sub>2</sub>O<sub>3</sub> electrode; CV curves of the α-MnO<sub>2</sub> electrode; cycling and rate performances of MnO<sub>2</sub>-Bi<sub>2</sub>O<sub>3</sub>-10 and α-MnO<sub>2</sub> electrodes; capacitive and diffusion-controlled contribution of MnO<sub>2</sub>-Bi<sub>2</sub>O<sub>3</sub>; enlargement of GITT profiles for MnO<sub>2</sub>-Bi<sub>2</sub>O<sub>3</sub>-10; GITT curves of α-MnO<sub>2</sub>; the SEM image of [Zn(OH)<sub>2</sub>]<sub>3</sub>ZnSO<sub>4</sub>·<i>x</i>H<sub>2</sub>O; XRD of Bi<sub>2</sub>O<sub>3</sub>-MnO<sub>2</sub>-10 at 1.3 V; SEM image of ZnMn<sub>2</sub>O<sub>4</sub>; Mn 2p of the MnO<sub>2</sub>-Bi<sub>2</sub>O<sub>3</sub>; the enlarged XRD spectrum of cycled MnO<sub>2</sub>-Bi<sub>2</sub>O<sub>3</sub>; cycling performance of Bi<sub>2</sub>Mn<sub>4</sub>O<sub>10</sub>; comparison between the electrochemical performance of this work with previously reported similar materials; and fitting results of MnO<sub>2</sub>-Bi<sub>2</sub>O<sub>3</sub>-10 and α-MnO<sub>2</sub> EIS measurements (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c01495/suppl_file/ae1c01495_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels