Microstructure and mechanical characterization of additively manufactured Fe11Cr8Ni5Co3Mo martensitic stainless steel
Lingzhi Wu,Dil Faraz Khan,Cong Zhang,Ruijie Zhang,Xue Jiang,Yongwei Wang,Geng Liu,Haiqing Yin,Jie Su,Xuanhui Qu
DOI: https://doi.org/10.1016/j.matchar.2023.113106
IF: 4.537
2023-06-28
Materials Characterization
Abstract:This study investigates the impact of various printing processes on the microstructure, grain orientation, dislocation density, residual stresses, and mechanical properties of Fe11Cr8Ni5Co3Mo0.2Si0.16Al0.12 V martensitic aged stainless steels produced through laser-based powder bed fusion (LPBF) using different processing parameters. The LPBF samples displayed varying densities, dislocation densities, and grain orientations with different combinations of process parameters. Sample 3 showed the highest densification effect, dislocation density ranged from 6.23 × 10 13 m −2 -1.164 × 10 14 m −2 . The horizontally crystallographic texture is primarily 〈111〉 orientation, it was observed that sample 3 also had a 〈001〉 orientation. The building direction has strong Gaussian texture {110} 〈001〉. The residual stress is compressive residual stress, and the maximum residual stress is depicted in sample 6, which is −222.8 ± 16.8 MPa. The optimal combination for the ultimate tensile strength and elongation was achieved using a laser power of 200 W, scanning speed of 1000 mm/s, hatch spacing of 100 μm, layer thickness of 30 μm, and laser energy density of 66.7 J/mm 3 . The total yield strength increase in the LPBF MSS samples, 60% can be attributed to the intensification of dislocations, with the contributions to intensity ranked in the order of σd > σt > σgb > σp .
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing