Abstract:The slow advance of a crack in sodo-silicate glasses was studied at nanometer scale by in situ and real time atomic force microscopy (AFM) in a well controlled atmosphere. An enhanced diffusion of sodium ions in the stress gradient field at the submicrometric vicinity of the crack tip was revealed through several effects: growth of nodules in AFM height images, changes in the AFM tip/sample energy dissipation. The nodules patterns revealed a dewetting phenomenon evidenced by 'breath figures'. Complementary chemical micro-analyses were done. These experimental results were explained by a two-step process: i) a fast migration (typical time: few milliseconds) of sodium ions towards the fracture surfaces as proposed by Langford et al. [J. Mat. Res. 6 (1991) 1358], ii) a slow backwards diffusion of the cations as evidenced in these AFM experiments (typical time: few minutes). Measurements of the diffusion coefficient of that relaxing process were done at room temperature. Our results strengthen the theoretical concept of a near-surface structural relaxation due to the stress-gradient at the vicinity of the crack tip. The inhomogeneous migration of sodium ions might be a direct experimental evidence of the presence of sodium rich channels in the silicate structure [A. Meyer et al., Phys. Rev. Let. 93 (2004) 027801].

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: in silicate glass, whether there is a stress - enhanced ion diffusion phenomenon near the crack tip, and to study the specific mechanism and characteristics of this phenomenon on the nanoscale through atomic force microscopy (AFM). Specifically, the research aims to explore the following aspects: 1. **Influence of stress gradient on sodium ion diffusion**: In the stress field near the crack tip, whether the rapid migration (millisecond - level) of sodium ions and the subsequent slow reverse diffusion (several minutes) will occur. Whether this diffusion phenomenon is related to the surface structure relaxation during the crack propagation process. 2. **Experimental verification**: Through AFM to observe in real - time the microstructure changes (such as nodule growth) formed during the crack propagation process, and combine with chemical micro - analysis (such as EPMA and SIMS) to verify whether these phenomena are related to the migration of sodium ions. 3. **Diffusion coefficient measurement**: Measure the sodium ion diffusion coefficient under room - temperature conditions to quantify this diffusion phenomenon and explore the influence of humidity on it. 4. **Theoretical explanation**: Try to explain the experimental results and propose a two - step process model: first, the rapid migration of sodium ions under the action of the stress field, and second, the slow recovery of the unbalanced sodium ion concentration. The core problem of the paper lies in understanding the influence of the stress field near the crack tip on the ion diffusion behavior, especially whether this diffusion will lead to changes in the crack propagation mechanism, thus providing a new perspective for understanding the fracture behavior of brittle materials.

Stress-enhanced ion diffusion at the vicinity of a crack tip as evidenced by atomic force microscopy in silicate glasses

Physically-based Interpretation of Abnormal Stress Relaxation Response in Glassy Polymers

Dynamic condensation of water at crack tips in fused silica glass

Diffusion-controlled crack propagation in alkali feldspar

Fracture of silicate glasses: Micro-cavities and correlations between atomic-level properties

A Kinship between the EGRET SNR's and Sgr A East

Fracture of glassy materials as detected by real-time Atomic Force Microscopy (AFM) experiments

Nanoscale damage during fracture in silica glass

Cracking in polymer glasses and evolution at zero stress: Highlighting discrete long time scale relaxations

Crack path instabilities in DCDC experiments in the low speed regime

Diffusive crack-grain interplay in freestanding nanocrystalline silver thin film

Glass breaks like metals, but at the nanometer scale

Crack arrest and stress dependence of laser-induced surface damage in fused-silica and borosilicate glass

In-situ observation of crack propagation through the nucleation of nanoscale voids in ultra-thin, freestanding Ag films

Stress-dependent Molecular Pathways of Silica–water Reaction

The Competing Effect of Initial Crack Depth Versus Chemical Strengthening Parameters on Apparent Fracture Toughness of Sodium Aluminosilicate Glass

Stress amplification and relaxation imaging around cracks in nanocomposite gels using ultrasound elastography

Roughness of oxide glass subcritical fracture surfaces

Crack-tip strain field mapping and the toughness of metallic glasses

Direct observation of pore collapse and tensile stress generation on pore wall due to salt crystallization

Sodium diffusion through amorphous silica surfaces: A molecular dynamics study