Temperature dependences of interface reactions and Tb diffusion behavior of Pr-Tb-Cu-Al alloys/Nd-Fe-B magnet

Kechao Lu,Xiaoqian Bao,Xinfang Song,Yanxin Wang,Minghui Tang,Jiheng Li,Xuexu Gao

DOI: https://doi.org/10.1016/j.scriptamat.2020.09.020

IF: 6.302

2021-01-01

Scripta Materialia

Abstract:<p>Interface reactions and structure of Pr_52.5Tb_17.5Cu₃₀, Pr₆₀Tb₂₀Al₂₀ and Pr₆₀Tb₁₀Cu₁₅Al₁₅ (at%) alloys with Nd-Fe-B magnets processed at various temperatures were systematically investigated. The alloys first melted and diffused through grain boundaries, and a higher temperature was required to form Tb-rich shells. Compared to Pr_52.5Tb_17.5Cu₃₀ and Pr₆₀Tb₂₀Al₂₀, Pr₆₀Tb₁₀Cu₁₅Al₁₅ with Al/Cu co-doping promoted Tb diffusion through grain boundaries especially at a lower temperature than 800 °C, and consequently developed continuous and thin Tb-rich grain boundaries. We presented two-step diffusion process with Pr₆₀Tb₁₀Cu₁₅Al₁₅, including low-temperature diffusion to accelerate Tb diffusion through grain boundaries and subsequent high-temperature diffusion to mainly promote Tb grain diffusion. Consequently, due to more homogeneous Tb distribution and resulting thinner Tb-rich grain boundaries, coercivity increment of 11 kOe was achieved by introducing only 0.33 wt% Tb, obviously lower than 0.48 wt% in conventional one-step diffusion magnet.</p>

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering