Enhancing the grain boundary diffusion efficiency of Tb for Nd-Fe-B magnets using multi-element composite diffusion source

Jing Pan,Shuai Cao,Yuhao Li,Qing Li,Guangfei Ding,Bo Zheng,Shuai Guo,Xiaodong Fan,Renjie Chen,Aru Yan

DOI: https://doi.org/10.1016/j.jallcom.2024.174003

IF: 6.2

2024-02-01

Journal of Alloys and Compounds

Abstract:Grain boundary diffusion of the heavy rare-earth element Tb, facilitated by multielement alloys, was investigated in Nd-Fe-B sintered magnets. This study systematically examined magnets treated with various diffusion sources: conventional TbH x powders, a mixture of TbH x and Pr45.0Cu18.3Al27.5Ga9.2 (at%) alloys, and integrated Tb10.0Pr35.0Cu18.3Al27.5Ga9.2 (at%) alloys. Results indicated that, although the total Tb content was considerably reduced from 2.80 to 0.49 wt%, the coercivities of the magnets employing multielement composite diffusion sources were still enhanced to a high level, comparable to those treated with TbH x alone. Notably, the coercivity of the magnets diffused with Tb10.0Pr35.0Cu18.3Al27.5Ga9.2 substantially increased to 24.14 kOe from the original value of 14.19 kOe, and the Tb utilization rate reached 73.47%. In addition, the coercivity increment per unit mass of Tb was 20.31 kOe/wt%. Microstructural observations and analyses of the diffusion process revealed that the assisted diffusion by the multielement composite effectively prevented superficial Tb accumulation, thereby enhancing diffusion efficiency. This process resulted in the formation of typical continuous grain boundaries and a core-shell structure. Furthermore, it was observed that low-melting-point metal elements, particularly Al, preferentially infiltrated the magnet interior and wetted the grain boundary channels during the early diffusion stages, facilitating efficient Tb diffusion. This study lays the groundwork for developing highly efficient magnets with reduced heavy rare-earth content.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper attempts to address the issue of improving the grain boundary diffusion efficiency of the heavy rare earth element Tb in sintered Nd-Fe-B permanent magnets, in order to reduce the total amount of Tb while maintaining or enhancing the coercivity (Hc) of the magnets. Specifically, the researchers aim to improve the diffusion effect of Tb through a multi-element composite diffusion source (including Tb, Pr, Cu, Al, Ga, etc.), thereby significantly enhancing the coercivity of the magnets while reducing the Tb content.

### Background and Issues
1. **Importance of Improving Coercivity**: Sintered Nd-Fe-B permanent magnets are widely used in high-tech fields such as wind power generation, medical equipment, and electric motors. In high-temperature environments, improving the coercivity of these magnets is crucial for enhancing their performance.
2. **Traditional Tb Diffusion Methods**: Typically, the coercivity is improved by introducing heavy rare earth elements (such as Tb) with high magnetic anisotropy fields (HA). However, in the traditional grain boundary diffusion (GBD) process, Tb tends to accumulate heavily on the surface of the magnet, leading to low utilization efficiency of Tb.
3. **Advantages of Multi-Element Composite Diffusion Sources**: By using multi-element composite diffusion sources, the diffusion path of Tb can be optimized, reducing surface accumulation of Tb and improving the diffusion efficiency and utilization rate of Tb.

### Research Objectives
1. **Reduce Total Amount of Tb**: Through the use of multi-element composite diffusion sources, reduce the total amount of Tb from 2.80 wt% to 0.49 wt%.
2. **Improve Coercivity**: Significantly enhance the coercivity of the magnets even with a substantial reduction in Tb content, achieving or surpassing the effects of traditional TbHx diffusion methods.
3. **Optimize Microstructure**: Form continuous grain boundary structures and uniform Tb-rich shells through multi-element composite diffusion sources, further improving the coercivity of the magnets.

### Experimental Methods
1. **Design of Diffusion Sources**: Designed a low-melting-point Pr45.0Cu18.3Al27.5Ga9.2 alloy, and mixed or integrated it with TbHx to form multi-element composite diffusion sources.
2. **Diffusion Experiments**: Coated different types of diffusion sources on the surface of the magnets, and after heat treatment, analyzed the changes in magnetic properties and microstructure of the magnets.
3. **Characterization Methods**: Characterized using pulsed field magnetometer (PFM), inductively coupled plasma optical emission spectrometer (ICP-OES), scanning electron microscope (SEM), energy-dispersive X-ray spectrometer (EDS), electron probe micro-analyzer (EPMA), and transmission electron microscope (TEM).

### Main Findings
1. **Significant Increase in Coercivity**: The coercivity of magnets using multi-element composite diffusion sources increased from 14.19 kOe to 24.14 kOe, with a Tb utilization rate of 73.47%, far higher than traditional methods.
2. **Microstructure Optimization**: Multi-element composite diffusion sources effectively prevented excessive accumulation of Tb on the surface, forming continuous grain boundary structures and uniform Tb-rich shells, improving the diffusion efficiency of Tb.
3. **Role of Low-Melting-Point Elements**: Particularly Al, which preferentially infiltrated into the magnet, wetting the grain boundary channels and promoting effective diffusion of Tb.

### Conclusion
Through multi-element composite diffusion sources, the coercivity of sintered Nd-Fe-B permanent magnets can be significantly improved while substantially reducing the amount of Tb used. This research provides an important theoretical and experimental basis for designing efficient multi-element diffusion sources and effectively utilizing heavy rare earth elements.