Sulfur dioxide sensing properties of MOF-derived ZnFe2O4 functionalized with reduced graphene oxide at room temperature

Lan-Juan Zhou,Xi-Xi Zhang,Wen-Yuan Zhang

DOI: https://doi.org/10.1007/s12598-020-01608-w

IF: 6.318

2020-10-27

Rare Metals

Abstract:<p class="a-plus-plus">In this paper, ZnFe<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">4</sub> nanorods were prepared using Zn/Fe metal organic framework (MOF) as precursors, and ZnFe<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">4</sub>/reduced graphene oxide (rGO) was prepared by hydrothermal method. The morphology and composition of the ZnFe<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">4</sub>/rGO nanocomposite were characterized, and the results showed that the MOF-derived ZnFe<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">4</sub> nanorods are uniformly modified on the surface of rGO. The ZnFe<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">4</sub>/rGO nanocomposite exhibits better SO<sub class="a-plus-plus">2</sub> gas sensing performance than the single ZnFe<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">4</sub> nanorods at room temperature. The sensing characteristics of single ZnFe<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">4</sub> film sensor, single rGO film sensor and ZnFe<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">4</sub>/rGO composite film sensor at SO<sub class="a-plus-plus">2</sub> gas concentration (1 × 10<sup class="a-plus-plus">−6</sup>–100 × 10<sup class="a-plus-plus">−6</sup>) were tested. The response of ZnFe<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">4</sub>/rGO composite sensor can reach 18.32% at room temperature. Compared with single ZnFe<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">4</sub> and rGO film sensors, the ZnFe<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">4</sub>/rGO composite sensor has better transient response, good sensitivity and selectivity. In this work, the improvement of the sensor performance is not only due to the p–n heterostructure between ZnFe<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">4</sub> nanorods and rGO nanosheets, but also to the excellent electrical properties of rGO. It provides a new idea for the detection of SO<sub class="a-plus-plus">2</sub> at room temperature.</p>

materials science, multidisciplinary,metallurgy & metallurgical engineering