Strengthening and Toughening Mechanism and Corrosion Resistance of 7003 Aluminum Alloy by Thermomechanical Treatment
Caiwei Xiang,Lingling Xie,Jinghui Li,Guangxin Luo,Jinxiu Fang,Hongbo Pan
DOI: https://doi.org/10.1007/s11665-024-10402-z
IF: 2.3
2024-11-20
Journal of Materials Engineering and Performance
Abstract:In this paper, the microstructure evolution, mechanical properties and corrosion behavior of 7003 aluminum alloy under dynamic aging (DYA, including rolling deformation and final aging) process were studied. The results show that with the increase in rolling reduction, the grain is refined, the dislocation density is gradually increased, and the high-angle grain boundary (HAGB) is continuously transformed into low-angle grain boundary (LAGB). At the same time, the strength, hardness and corrosion resistance of the alloy are significantly improved, but the plasticity is significantly reduced. In the first stage of strain hardening, the accumulation of geometrically necessary dislocations (GNDs) hinders the slip of dislocations in the tensile direction, so that the alloy exhibits a high strain hardening rate at the initial stage of deformation. With the increase in plastic strain, the work hardening ability of the deformed alloy gradually decreases. The improvement of the yield strength of the alloy is mainly attributed to dislocation strengthening and precipitation strengthening, and the contribution of grain boundary strengthening is the smallest. In the corrosion experiment, the grain refinement increases the bonding force of the interface to form a dense oxide film. After the introduction of the DYA process, the discontinuously distributed grain boundary precipitates (GBPs) gradually coarsen, and the η phase acts as a capture point to make the hydrogen bubble nucleate, reducing the accumulation of hydrogen atoms at the crack tip, resulting in the continuous enhancement of the corrosion resistance of the alloy. Therefore, the improvement of corrosion resistance is mainly due to grain refinement, discontinuous distribution of coarse GBPs and narrow precipitate-free zone (PFZ).
materials science, multidisciplinary