Performance Assessment of a New Flat Sepiolite Clay-Based Ultrafiltration Membrane for the Removal of Paracetamol and Indigo Blue Dyes from Two Synthetic Aqueous Solutions

Mohamed Romdhani,Wala Aloulou,Hajer Aloulou,Joelle Duplay,Catherine Charcosset,Raja Ben Amar
DOI: https://doi.org/10.3390/su16051860
IF: 3.9
2024-02-24
Sustainability
Abstract:In the last decade, the development of a new generation of membranes based on low-cost materials has been widely studied. These membranes demonstrate significantly higher performance than the conventional ceramic membranes currently used in membrane separation technology. This work is focused on the development of a low-cost flat UF ceramic membrane composed completely of sepiolite using a uniaxial pressing method with dimensions of 5.5 cm of diameter and 3 mm of thickness. The sintering temperatures used were from 650 to 800 °C. Several properties, such as morphology, porosity, permeability, mechanical strength, and chemical resistance, are investigated. The results show that the mean pore diameter is increased from 40 to 150 nm when the sintering temperature increases from 650 °C to 800 °C. At these temperatures, excellent mechanical strength of 18 MPa to 22 MPa and high chemical resistance were achieved. SEM results revealed a crack-free structure with a uniformly smooth surface. Permeability tests were conducted using dead-end filtration. The sepiolite membrane demonstrated an improvement in its water permeability from 18 to 41 L·m−2·h−1·bar−1 when the sintering temperature increased from 650 °C to 750 °C. The efficiency of the sepiolite membranes sintered at 650 °C and 700 °C were evaluated with the application of the removal of paracetamol (PCT) and indigo blue (IB) dye separately from two synthetic aqueous solutions representing the pharmaceutical and textile sectors. Excellent removal efficiency of almost 100% for both contaminants was observed at ambient temperature and a pressure of 3 bars. Membrane regeneration was achieved through simple rinsing with deionized water. According to this finding, the UF sepiolite membrane demonstrated reversible fouling, which is consistent with the fouling coefficient "FRR" value higher than 90%.
environmental sciences,environmental studies,green & sustainable science & technology
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to develop a low - cost flat - shaped sepiolite - based ultrafiltration membrane and evaluate its performance in removing paracetamol (PCT) and indigo dye (IB) from synthetic aqueous solutions. Specifically, the research objectives include: 1. **Develop a new - type ceramic membrane**: Researchers prepared a flat - shaped ultrafiltration membrane composed entirely of sepiolite by uniaxial pressing method. The diameter of this membrane is 5.5 cm and the thickness is 3 mm. This membrane was sintered in the temperature range of 650 - 800 °C. 2. **Evaluate the performance of the membrane**: Researchers tested various properties of the membrane, including morphology, porosity, permeability, mechanical strength and chemical stability. The results show that as the sintering temperature increases, the average pore size increases from 40 nm to 150 nm, the mechanical strength reaches 18 - 22 MPa, and the chemical stability is good. 3. **Efficiency of removing pollutants**: Researchers carried out removal experiments on paracetamol and indigo dye in two synthetic aqueous solutions using this membrane. The results show that at normal temperature and under a pressure of 3 bar, the removal efficiency of these two pollutants is close to 100%. 4. **Regeneration ability of the membrane**: By simply rinsing with deionized water, the membrane can restore its initial performance, indicating that the membrane has reversible fouling characteristics and the fouling recovery rate (FRR) value exceeds 90%. In general, this research aims to develop an efficient and low - cost sepiolite - based ultrafiltration membrane for treating wastewater containing organic and inorganic pollutants, especially in the wastewater generated in the pharmaceutical and textile industries.