Semiconductive and Photoconductive Properties of the Single Molecule Magnets Mn12-Acetate and Fe8Br8

J. M. North,D. Zipse,N. S. Dalal,E. S. Choi,E. Jobiliong,J. S. Brooks,D. L. Eaton

DOI: https://doi.org/10.48550/arXiv.cond-mat/0301515

2003-01-28

Abstract:Resistivity measurements are reported for single crystals of Mn12-Acetate and Fe8Br8. Both materials exhibit a semiconductor-like, thermally activated behavior over the 200-300 K range. The activation energy, Ea, obtained for Mn12-Acetate was 0.37 +/- 0.05 eV, which is to be contrasted with the value of 0.55 eV deduced from the earlier reported absorption edge measurements and the range of 0.3-1 eV from intramolecular density of states calculations, assuming 2Ea = Eg, the optical band gap. For Fe8Br8, Ea was measured as 0.73 +/- 0.1 eV, and is discussed in light of the available approximate band structure calculations. Some plausible pathways are indicated based on the crystal structures of both lattices. For Mn12-Acetate, we also measured photoconductivity in the visible range; the conductivity increased by a factor of about eight on increasing the photon energy from 632.8 nm (red) to 488 nm (blue). X-ray irradiation increased the resistivity, but Ea was insensitive to exposure.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to understand the electrical transport properties of single - molecule magnets (Single Molecule Magnets, SMMs) Mn12 - Acetate and Fe8Br8. Specifically, the authors focus on the following aspects:

1. **Semiconductor and photoconductive properties**: Study the resistivity changes of these materials in the temperature range of 200 - 300 K to determine whether they exhibit semiconductor behavior and measure their activation energy (\(E_a\)).

2. **Photoconductivity**: Study the photoconductivity of Mn12 - Acetate in the visible light range and explore the influence of photons of different wavelengths on its electrical conductivity.

3. **X - ray irradiation effects**: Study the effects of X - ray irradiation on the resistivity and activation energy of Mn12 - Acetate to understand the role of defects in electrical transport properties.

### Research background

Mn12 - Acetate and Fe8Br8 are two important single - molecule magnets with the phenomenon of Macroscopic Quantum Tunneling (MQT). These materials exhibit unique hysteresis loops and magnetization relaxation characteristics at low temperatures, making them potential candidates for molecular - size memories and quantum computing elements. However, although the magnetic and optical properties of these materials have been widely studied, their electrical transport properties have been rarely reported.

### Main findings

1. **Resistivity measurement**:
- Mn12 - Acetate exhibits typical semiconductor behavior in the range of 200 - 300 K, with an activation energy of \(E_a = 0.37\pm0.05\) eV.
- Fe8Br8 also exhibits semiconductor behavior in the same temperature range, with an activation energy of \(E_a = 0.73\pm0.1\) eV, which is significantly higher than that of Mn12 - Acetate.

2. **Photoconductivity**:
- Mn12 - Acetate exhibits significant photoconductivity in the visible light range. As the photon energy increases from 632.8 nm (red light) to 488 nm (blue light), the electrical conductivity increases by about 8 times. This indicates that photon absorption leads to an increase in carrier concentration.

3. **X - ray irradiation effects**:
- X - ray irradiation increases the resistivity of Mn12 - Acetate, but the activation energy \(E_a\) is insensitive to irradiation, indicating that the defects introduced by irradiation mainly act as carrier traps rather than changing the basic electrical transport mechanism.

### Conclusion

Through resistivity, photoconductivity and X - ray irradiation experiments, the authors confirm that Mn12 - Acetate and Fe8Br8 exhibit semiconductor behavior near room temperature, and the photoconductivity of Mn12 - Acetate is closely related to the carrier generation mechanism in its structure. Further research needs to combine theoretical calculations to more deeply understand the electrical transport paths and mechanisms of these materials.