Engineering sphere-like porous FeF3@C cathode with rational interfacial designing towards high-power batteries
Ming-Jun Jing,Jun-Chang Liu,Shao-Hui Yuan,Wen-Qing Zhao,Min Liu,Yan-Song Bai,Peng Ge,Tian-Jing Wu
DOI: https://doi.org/10.1007/s12598-022-02137-4
IF: 6.318
2022-12-06
Rare Metals
Abstract:Due to the high theoretical capacity and energy density, conversion-type metal fluorides have captured plenty of attentions but still suffer from the inferior kinetic behaviors and serious capacity fading. For addressing the issues above, the strategies of surface/interface engineering are utilized for the preparation of sphere-like porous FeF 3 @C materials, where the as-resulted sample displays the uniform particle size (~ 150 nm in radii) and the ultra-thin carbon layers (thickness of ~ 10 nm). Significantly, benefitting from the rich oxygen of precursor, the interfacial chemical bonds FeOC are successfully constructed between carbon matrix and FeF 3 materials, accompanying by the enhancements of ions/electrons (e) conductivity and stability. When used as Li-storage cathodes, the initial lithium-ions storage capacity could reach up to ~ 400 mAh·g −1 at 0.1 A·g −1 . Even at 1.0 A·g −1 , the capacity could be still remained at about 210 mAh·g −1 , with the retention of 85% after 400 cycles. Assisted by the detailed kinetic behaviors, the considerable electrochemical properties come from the enhanced diffusion-controlled contributions, whilst the segregation of Fe with LiF is effectively alleviated by unique architecture. Moreover, during cycling, solid electrolyte interface film is reversibly formed/decomposed. Thus, this work is expected to offer rational exterior/interfacial designing strategies for metal-based samples.
materials science, multidisciplinary,metallurgy & metallurgical engineering