Frequency Сonversion of Femtosecond Ti:sapphire Laser Pulse to the Long-wave Mid-IR Range with BaGa2GeSe6 Crystal

Kinyaevskiy, I. O.

DOI: https://doi.org/10.1134/s0021364024600988

2024-05-14

JETP Letters

Abstract:Generation of ultrashort mid-IR pulses spanning from 8.5 to 10.5 μm with high energy (up to 4.5 μJ) was experimentally demonstrated through difference frequency generation in BaGa 2 GeSe 6 crystal pumped by 100-fs 0.95-μm Ti:sapphire laser pulses. Optical damage threshold and two-photon absorption coefficient were determined for this pump pulses. Frequency conversion efficiency reached 0.24% at 1.85 mJ pump pulse energy and was decreased at higher one. Estimations indicate that application of 15 mm in diameter wide-aperture BaGa 2 GeSe 6 sample will allow one to increase pump pulse energy up to ~10 mJ, and to increase the mid-IR pulse energy up to 24 μJ at the same efficiency.

physics, multidisciplinary

What problem does this paper attempt to address?

The paper primarily explores the technology of converting femtosecond Ti:sapphire laser pulses to the long-wave mid-infrared (mid-IR) range using BaGa₂GeSe₆ (BGGSe) crystals. Specifically, the research team achieved the generation of ultrashort mid-IR pulses in the range of 8.5 to 10.5 micrometers with energies up to 4.5 microjoules in BGGSe crystals through Difference Frequency Generation (DFG) technology.

The main objective of the research is to develop a long-wave mid-IR femtosecond laser system capable of producing microjoule-level energy with peak power exceeding the self-focusing critical power of solid materials (tens of megawatts). To achieve this goal, the researchers selected a femtosecond Ti:sapphire laser as the front-end laser source and used BGGSe crystals as the nonlinear medium for frequency conversion, due to their appropriate transmittance, high nonlinearity, favorable dispersion characteristics, and high optical damage threshold.

Experimental results show that with a pump pulse energy of 1.85 millijoules, the frequency conversion efficiency reached 0.24%. It is anticipated that using a large-aperture BGGSe crystal sample with a diameter of approximately 15 millimeters could increase the pump pulse energy to about 10 millijoules, while increasing the mid-IR pulse energy to around 24 microjoules, maintaining the same conversion efficiency.

Additionally, the paper compares the performance differences between BGGSe crystals and traditional AgGaS₂ (AGS) crystals in the experiments, and provides a detailed description of the experimental setup and process, as well as characterizing the optical properties of the BGGSe crystals.