U. Geiersbach,A. Bergmann,K. Westerholt
Abstract:We report on the preparation of thin films and multilayers of the intermetallic Heusler compound CuMnAl, Co2MnSn, Co2MnSi and Co2MnGe by rf-sputtering on MgO and Al2O3 substrates. Cu2MnAl can be grown epitaxially with (100)-orientation on MgO (100) and in (110)-orientation on Al2O3 a-plane. The Co based Heusler alloys need metallic seedlayers to induce high quality textured growth. We also have prepared multilayers with smooth interfaces by combining the Heusler compounds with Au and V. An analysis of the ferromagnetic saturation magnetization of the films indicates that the Cu2MnAl-compound tends to grow in the disordered B2-type structure whereas the Co-based Heusler alloy thin films grow in the ordered L21 structure. All multilayers with thin layers of the Heusler compounds exhibit a definitely reduced ferromagnetic magnetization indicating substantial disorder and intermixing at the interfaces.
What problem does this paper attempt to address?
The problems that this paper attempts to solve mainly focus on the following aspects:
1. **Preparation of high - quality Heusler compound thin films and multilayers**:
- The paper studied the preparation and structural characteristics of thin films and multilayers of Heusler compounds such as Cu₂MnAl, Co₂MnSn, Co₂MnSi and Co₂MnGe on MgO and Al₂O₃ substrates. These materials have unique magnetic and electrical properties, especially having potential applications in the field of spintronics.
2. **Improvement of the crystallization quality and magnetic properties of thin films**:
- By using metal seed layers (such as Au, V, etc.), the researchers were able to induce high - quality textured growth, thereby improving the crystallization quality of the thin films. Especially for Co - based Heusler alloys, this method significantly improved their structure and magnetic properties.
3. **Study of the magnetic behavior of thin films and multilayers**:
- The researchers measured the saturation magnetization of thin films and multilayers and discovered some interesting magnetic phenomena. For example, Cu₂MnAl thin films tend to form a disordered B2 - type structure, while Co - based Heusler alloys are more likely to form an ordered L2₁ structure. In addition, the interface effect in multilayers led to a significant change in magnetism, especially in the case of extremely thin layers, where the magnetism was significantly reduced.
4. **Exploration of the application potential of Heusler compounds in spintronic devices**:
- The paper explored the application potential of these materials in spin - transport devices, especially their performance in giant magnetoresistance (GMR) and tunnel magnetoresistance (TMR) devices. The experimental results showed that although these materials theoretically have ideal spin - polarization characteristics, in practical applications, due to disorder and alloying at the interface, the magnetic and spin - polarization properties will be affected.
### Formula summary
- **Superlattice periodicity calculation formula**:
\[
\Lambda = l \cdot \frac{\lambda}{2\left(\sqrt{\Theta_l^2 - \Theta_c^2}\right)}
\]
where \( \Lambda \) is the superlattice periodicity, \( l \) is the reflection order, \( \lambda \) is the X - ray wavelength, and \( \Theta_l \) and \( \Theta_c \) are the \( l \)-th - order reflection angle and the critical angle, respectively.
- **Superlattice periodicity calculation formula from satellite peak positions**:
\[
\Lambda = \frac{\lambda}{2 \cdot l \cdot \Delta(\Theta) \cdot \cos(\Theta)}
\]
where \( \Delta(2\Theta) \) is the angular separation between the satellite peak and the fundamental Bragg peak.
- **Coherent length calculation formula (Scherrer equation)**:
\[
D_{coh} = \frac{\lambda}{\Delta(2\Theta) \cdot \cos(\Theta)}
\]
where \( D_{coh} \) is the coherent length and \( \Delta(2\Theta) \) is the full width at half - maximum (FWHM) of the satellite peak.
Through the research on these problems, the paper provides an important experimental basis and theoretical guidance for the further application of Heusler compounds in the field of spintronics.