Structure, Structural Relaxation and Ion Transport in Sodium Disilicate Melts

A. Meyer,H. Schober,D.B. Dingwell

DOI: https://doi.org/10.48550/arXiv.cond-mat/0206168

2002-06-11

Abstract:We have investigated Na2SiO5 melts with inelastic neutron scattering at temperatures up to 1600K. The Si-O network relaxes on a time scale of ns, whereas the Na ion relaxation dynamics are found on a time scale of 10ps. The elastic structure factor exhibits at ~0.9A-1 an emerging prepeak which becomes more pronounced with increasing temperature. The prepeak is caused by the formation of sodium rich regions in the partially disrupted Si-O tetrahedral network.

Materials Science,Disordered Systems and Neural Networks

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to understand the structural and dynamic characteristics of sodium disilicate melt (Na₂Si₂O₅) at high temperatures, especially the change of its elastic structure factor with temperature and its influence on the ionic diffusion behavior. Specifically, the research aims to reveal the following aspects:

1. **Structural changes**: As the temperature rises, especially under conditions far above the glass transition temperature \(T_g\), the elastic structure factor of the sodium disilicate melt changes significantly. In particular, an obvious pre - peak appears at the wave vector \(q\approx0.9\,\text{\AA}^{-1}\), which indicates that sodium - rich regions are formed in the melt.

2. **Dynamic characteristics**: The dynamic processes of structural relaxation and ionic diffusion in the melt were studied. Through neutron inelastic scattering experiments, the structural relaxation time scale of the partially destroyed Si - O tetrahedral network was determined to be on the order of nanoseconds, while the diffusion time scale of sodium ions was on the order of picoseconds.

3. **Microscopic mechanisms**: The formation of sodium - rich regions and their influence on the melt viscosity and ionic transport were explored. Studies have shown that the existence of sodium - rich regions may lead to a weak dependence of the melt viscosity on temperature, especially at higher temperatures.

### Main findings

- **Change in elastic structure factor**: As the temperature rises, the elastic structure factor \(S(q,\omega = 0)\) shows an obvious pre - peak at \(q\approx0.9\,\text{\AA}^{-1}\), which is attributed to the sodium - rich regions formed in the melt.

- **Structural relaxation time scale**: By fitting the experimental data, it was found that the structural relaxation time of the partially destroyed Si - O tetrahedral network is approximately 4 nanoseconds, and the relaxation process is non - exponential, with a stretched exponential \(\beta\approx0.75\).

- **Sodium ion diffusion time scale**: The diffusion time scale of sodium ions is approximately 10 picoseconds, and the diffusion dynamics exhibits non - exponential behavior, with the stretched exponential \(\beta\) between [0.7, 0.8].

These results not only provide new insights into the microstructure and dynamics of sodium disilicate melts, but also provide important experimental bases for further understanding the properties of magma in volcanic activities and the synthesis of technical glasses.