Abstract:In this study, hydrous manganese dioxide (HMO) modified poly(sodium acrylate) (PSA) hydrogel was produced for the first time to remove tetracycline(TC) and lead(Pb(II)) from water. The as-prepared composite was characterized using various techniques, such as SEM-EDS, FTIR, XRD, BET, and XPS, to elucidate the successful loading of HMO and analyze subsequent sorption mechanisms. Different influencing parameters such as adsorbent dose, initial concentration of adsorbates, reaction time, solution pH, and temperature were also investigated. The adsorption kinetic studies of both TC and Pb(II) removal indicated that equilibrium was achieved within 12 h, with respective removal rates of 91.9 and 99.5%, and the corresponding adsorption data were fitted to the second-order kinetics model. According to the adsorption isotherm studies, the sorption data of TC best fitted to the Langmuir isotherm model while the adsorption data of Pb(II) were explained by the Freundlich isotherm model. The maximum adsorption capacities of both TC and Pb(II) were found to be 475.8 and 288.7 mg/g, respectively, demonstrating excellent performances of the adsorbent. The uptake capacity of PSA-HMO was significantly influenced by the level of solution pH, in which optimum adsorption amount was realized at pH 4.0 in the TC and Pb(II) systems, respectively. Thermodynamic studies showed the process of TC and Pb(II) adsorptions were endothermic and spontaneous. Overall this study elucidated that PSA-HMO composite can be a promising candidate for antibiotics and heavy metal removal in water treatment applications.
What problem does this paper attempt to address?
The paper aims to address the issue of antibiotic (tetracycline, TC) and heavy metal lead (Pb(II)) pollution in water. Specifically, the researchers developed a novel hydrated manganese dioxide (HMO) modified sodium polyacrylate (PSA) hydrogel composite to enhance the removal efficiency of TC and Pb(II). Below is a summary of the main content of the paper:
### Research Background
With the rapid development of global industrialization and urbanization, the discharge of toxic pollutants (especially heavy metals and antibiotics) poses a serious threat to clean water resources. Lead (Pb(II)) has received widespread attention due to its harmful effects on human health and ecosystems. Tetracycline (TC), as the second most widely produced and used antibiotic, is extensively applied in clinical medicine, veterinary medicine, and the animal feed industry. However, TC has a low metabolic rate in organisms, and most unmetabolized TC is excreted into the environment through feces and urine, leading to the proliferation of antibiotic resistance genes in the environment. Therefore, it is particularly important to effectively remove TC and Pb(II) from water.
### Research Objectives
The main objective of this study is to synthesize a novel HMO-modified PSA hydrogel composite (PSA-HMO) and evaluate its performance in removing TC and Pb(II) from water. Specific goals include:
1. Synthesizing the PSA-HMO composite adsorbent and studying its structural, chemical, and physical properties.
2. Systematically investigating the adsorption behavior of TC and Pb(II) in single and binary systems, examining the effects of pH, initial concentration, equilibrium reaction time, and temperature.
3. Exploring adsorption isotherms, kinetics, and thermodynamic models.
4. Investigating the potential mechanisms of PSA-HMO in removing TC and Pb(II).
### Experimental Methods
1. **Material Preparation**: The PSA-HMO composite material was synthesized through ion exchange and reduction steps.
2. **Characterization Methods**: Techniques such as SEM-EDS, XRD, BET, FTIR, and XPS were used to characterize the composite material.
3. **Experimental Process**: The adsorption performance under different conditions (such as pH, initial concentration, reaction time, temperature) was studied, and adsorption isotherms, kinetics, and thermodynamic analyses were conducted.
### Main Results
1. **Structural and Morphological Characteristics**:
- SEM-EDS analysis showed that the PSA-HMO surface was covered with a large number of HMO particles, providing potential active adsorption sites.
- XRD analysis indicated that HMO was successfully loaded onto the PSA hydrogel, forming an amorphous structure.
- FTIR and XPS analyses revealed the functional groups on the PSA-HMO surface and their interaction mechanisms with TC and Pb(II).
2. **Adsorption Performance**:
- At a pH of 4.0, PSA-HMO exhibited optimal adsorption performance for TC, with a removal rate of up to 82.06%.
- At a pH of 4.0, PSA-HMO exhibited optimal adsorption performance for Pb(II), with a removal rate of up to 98.76%.
- The adsorption kinetics conformed to the second-order kinetic model, and the adsorption isotherms conformed to the Langmuir and Freundlich models, respectively.
3. **Thermodynamic Analysis**:
- Thermodynamic studies indicated that the adsorption process of TC and Pb(II) was endothermic and spontaneous.
### Conclusion
The PSA-HMO composite material demonstrated excellent performance in removing TC and Pb(II) from water, with high adsorption capacity and good selectivity. This material holds promise for widespread application in wastewater treatment.