Superconducting Bulk Magnets: Very High Trapped Fields and Cracking

S. Gruss,G. Fuchs,G. Krabbes,P. Verges,G. Stover,K.-H. Muller,J. Fink,L. Schultz

DOI: https://doi.org/10.1063/1.1413502

2001-04-20

Abstract:Improved trapped fields are reported for bulk melt-textured YBa2Cu3O7-x (YBCO) material in the temperature range between 20 K and 50 K. Trapped fields up to 12.2 T were obtained at 22 K on the surface of single YBCO disks (with Ag and Zn additions). In YBCO mini-magnets, maximum trapped fields of 16 T (at 24 K) and of 11.2 T (at 47 K) were achieved using (Zn + Ag) and Zn additions, respectively. In all cases, the YBCO disks were encapsulated in steel tubes in order to reinforce the material against the large tensile stress acting during the magnetizing process and to avoid cracking. We observed cracking not only during the magnetizing process, but also as a consequence of flux jumps due to thermomagnetic instabilities in the temperature range betweeen 20 K and 30 K.

Superconductivity

What problem does this paper attempt to address?

This paper aims to solve the problems encountered when the high - temperature superconductor YBa₂Cu₃O₇₋δ (YBCO) is used as a bulk magnet under low - temperature conditions (20K to 50K), especially how to increase its trapped magnetic field strength and prevent the material from cracking. Specifically:

1. **Increasing the trapped magnetic field strength**: Researchers improve the pinning and mechanical properties of YBCO materials by adding zinc (Zn) and silver (Ag) to achieve a higher trapped magnetic field strength. The experimental results show that at a temperature of 22K, a trapped magnetic field as high as 12.2 Tesla (T) is obtained on the surface of a single YBCO disk; in a mini - magnet composed of two YBCO disks, maximum trapped magnetic fields of 16T and 11.2T are achieved at temperatures of 24K and 47K respectively through (Zn + Ag) and Zn addition.

2. **Preventing material cracking**: In order to prevent the YBCO material from cracking due to the large tensile stress during the magnetization process, the researchers adopted the method of encapsulating the YBCO disk in a steel pipe. The steel pipe generates compressive stress on YBCO during the cooling process, which effectively compensates for the tensile stress during the magnetization process, improves the tensile strength of the material, and thus avoids the cracking phenomenon.

In addition, the paper also explores the problem of flux jumps due to thermomagnetic instability in the temperature range of 20K to 30K. These problems may cause damage to the YBCO disk during the heating process. The research results show that optimizing the heating rate can partially alleviate this problem, but a high trapped magnetic field may still cause irreversible material damage.

In summary, the main objective of this paper is to achieve a high trapped magnetic field at a higher temperature and solve the cracking problem of the material during use by improving the composition and structure of the YBCO material.