Characterization of Novel Cellulosic Salvadora Persica Fiber for Potentiality in Polymer Matrix Composites

Jamaluddin Hindi,Abdul Ajees Abdul Salam,Muralishwara K,Gurumurthy B M,Shivaprakash Y M,Ayman Ibrahim

DOI: https://doi.org/10.1080/15440478.2024.2409874

2024-10-05

Journal of Natural Fibers

Abstract:Natural fiber is expected to make polymer composites light and environmentally friendly. In this paper Salvadora persica natural fiber is characterized in view of its use in composite materials for the first time. Average diameter of the fiber was 250 μm and density was 1.3 g/cm 3 . The surface of the fiber was irregular with impurities and surface features such as shallow tubs, cell walls and lignin were revealed by Scanning Electron Microscopy (SEM). X-ray diffraction (XRD) analysis reveals Crystallinity Index (C.I) of 58% and Crystallite Size of 3.58 nm. The chemical bonds pertaining to different constituents of the natural fiber such as cellulose, hemicellulose and lignin were identified by Fourier Transform Infrared (FTIR) spectroscopic analysis. In the thermal degradation of the fiber during the Thermogravimetric analysis (TGA), three stages were identified. The maximum thermal degradation temperature (T final ) was determined to be 357°C. Tensile strength, Young's modulus and percentage elongation of the fiber were 430 ± 100 MPa, 16 ± 3.9 GPa and 4.2 ± 0.91% respectively. 天然纤维有望使聚合物复合材料轻便环保。本文首次对萨尔瓦多波斯天然纤维在复合材料中的应用进行了表征. 纤维的平均直径为250 μm,密度为1.3 g/cm3. 扫描电镜(SEM)显示,纤维表面不规则,有杂质和表面特征,如浅槽、细胞壁和木质素. X射线衍射(XRD)分析显示结晶指数(C.I)为58%,晶粒尺寸为3.58 nm. 通过傅里叶变换红外光谱(FTIR)分析,鉴定了天然纤维中纤维素、半纤维素和木质素等不同成分的化学键. 在热重分析(TGA)过程中,纤维的热降解分为三个阶段. 最大热降解温度(Tfinal)被确定为357°C. 纤维的抗拉强度、杨氏模量和伸长率分别为430 ± 100MPa、16 ± 3.9GPa和4.2 ± 0.91%.

materials science, textiles