Electrospinning core‐shell nanofibers for interfacial toughening and self‐healing of carbon‐fiber/epoxy composites

Xiang-fa Wu,Arifur Rahman,Zhengping Zhou,D. D. Pelot,S. Sinha-Ray,Bin Chen,Scott A. Payne,A. Yarin

DOI: https://doi.org/10.1002/APP.38838

2013-08-05

Abstract:This article reports a novel hybrid multiscale carbon-fiber/epoxy composite reinforced with self-healing core-shell nanofib- ers at interfaces. The ultrathin self-healing fibers were fabricated by means of coelectrospinning, in which liquid dicyclopentadiene (DCPD) as the healing agent was enwrapped into polyacrylonitrile (PAN) to form core-shell DCPD/PAN nanofibers. These core-shell nanofibers were incorporated at interfaces of neighboring carbon-fiber fabrics prior to resin infusion and formed into ultrathin self- healing interlayers after resin infusion and curing. The core-shell DCPD/PAN fibers are expected to function to self-repair the interfa- cial damages in composite laminates, e.g., delamination. Wet layup, followed by vacuum-assisted resin transfer molding (VARTM) technique, was used to process the proof-of-concept hybrid multiscale self-healing composite. Three-point bending test was utilized to evaluate the self-healing effect of the core-shell nanofibers on the flexural stiffness of the composite laminate after predamage fail- ure. Experimental results indicate that the flexural stiffness of such novel self-healing composite after predamage failure can be com- pletely recovered by the self-healing nanofiber interlayers. Scanning electron microscope (SEM) was utilized for fractographical analy- sis of the failed samples. SEM micrographs clearly evidenced the release of healing agent at laminate interfaces and the toughening and self-healing mechanisms of the core-shell nanofibers. This study expects a family of novel high-strength, lightweight structural polymer composites with self-healing function for potential use in aerospace and aeronautical structures, sports utilities, etc. V C 2012

Materials Science