Study on Blending Modification of Bisphenol A Epoxy
Xiaotao Fu,Long Ma,Lincong Chen,Cong Zhang,Xiaolin Chen,Xinran Li,Fangda Fu,Chuanfu Fu,Taobei Lin,Wensheng Mao
DOI: https://doi.org/10.3390/polym15153263
IF: 5
2023-08-01
Polymers
Abstract:Epoxy-resin-based composites in the field of current electrical materials often work in high temperature, high humidity or salt spray conditions. In order to improve the operation reliability of the composite insulator cross arm in a high temperature, high humidity and high salt spray environment, and analyze the aging mechanism and performance characteristics of resin, in this paper, wet heat aging and salt spray aging experiments were carried out on the blended resin system composed of bisphenol A type epoxy resin (E-51), aliphatic epoxy modified bisphenol A epoxy resin (2021P/E-51) and dimeric acid modified bisphenol A epoxy resin (EPD-172/E-51). Among them, 10 wt% and 20 wt% of 2021P blend resin and 10 wt% of EPD blend resin have superior thermo-mechanical properties. Under humid and hot conditions, the dielectric loss of 10 wt% EPD blend system before and after aging is 39.9% and 49.5% lower than that of pure E51 resin system, respectively. Under the condition of salt spray, the dielectric loss of 20 wt% and 10 wt% EPD blends decreased by 73.1% and 74.6% after aging. The leakage current of 10 wt% 2021P blend resin and 10 wt% EPD blend resin decreased by 7% and 3.8% before aging, respectively. After aging, they decreased by 3.7% and 2.2%, respectively. The bending strength of 2021P blend resin before and after aging reached 29.3 MPa and 26.6 MPa, respectively. The above three blending resin systems exhibit good electrical properties and good mechanical properties, their ageing resistance performance is strong and they are suitable as the matrix resin of compound cross arm mandrel material.
polymer science