Abstract:Recently, lattice-matched Zn 0.46 Cd 0.54 Se/ZnCdMgSe multiple-quantum-wells (MQWs) have been recognized as very promising materials to fabricate intersubband (ISB) devices such as quantum cascade lasers and mid-infrared photoconductors. These structures have important applications in biological and chemical detections. The ISB transition covers a wide mid-infrared wavelength range from 1.3 µm to a few tens of µm. In this work, two heavily doped n-Zn 0.46 Cd 0.54 Se/Zn 0.24 Cd 0.25 Mg 0.51 Se MQW structures have been grown on InP (001) substrate by molecular beam epitaxy. Temperature dependent steady-state photoluminescence (SSPL), temperature dependent time- resolved photoluminescence (TRPL), and Fourier transform infrared spectroscopy (FTIR) were performed to characterize their interband and ISB properties. These two MQW samples have similar structures except different well widths and different number of periods. The integrated SSPL intensities and the PL decay times of the MQWs were measured as functions of temperature in the range from 77 K to 290 K. The luminescence efficiency of the sample with 28 Å well width is larger than that of the sample with 42 Å well width although both samples exhibit similar temperature dependence of PL intensity. Time-resolved PL measurements show that the PL decay times of both samples decrease with increasing temperature. From 77 K to 290 K, the decay time of the sample with 28 Å well width is in the range of 440 ps ~ 120 ps and is much longer than that of the sample with 42 Å well width, which is in the range of 65 ps ~ 25 ps. Strong non-radiative recombinations dominate the luminescence behavior of the wider MQWs. Intersubband absorption spectra of the samples were measured by FTIR and show peak absorption at wavelengths of 3.99 µm and 5.35 µm for the MQWs with well widths of 28 Å and 42 Å, respectively, falling within the 3–5 µm range, which is of great interest for the infrared photodetector applications.

128X1 GaAs/AlGaAs multiple quantum well infrared detector array

GaAs/AlGaAs Quantum-Well Infrared Photodetectors on GaAs-on-Si Substrates

Photocurrent Spectra of Very Long Wavelength GaAs/AlGaAs Quantum Well Infrared Photodetector

Very long wave infrared quantum cascade detector with a twin-well absorption region

Multiple Quantum Barrier Avalanche Photodiode Based on GaN/AlGaN Heterostructures for Long Wavelength Infrared Detection

Photoelectric properties of two-color GaAs/GaAlAs quantum well infrared photodetectors

In X Ga 1−x As/Al Y Ga 1−y As/Al Z Ga 1−z As Asymmetric Step Quantum-Well Middle Wavelength Infrared Detectors

Study on Grating'Coupling Very Long Wavelength Gaas/Algaas Qwip

A Sensitive Double Quantum Well Infrared Phototransistor

Photocurrents of 14 Μm Quantum-Well Infrared Photodetectors

Van der Waals mid-wavelength infrared detector linear array for room temperature passive imaging

Linear array of charge sensitive infrared phototransistors for long wavelength infrared detection

Development of 64 X 64 Gaas/Algaas Mqw Long-Wave Infrared Fpas

15μm Quantum Well Infrared Photodetector for thermometric imagery in cryogenic windtunnel

Development of a High Performance 1280×1024 InGaAs SWIR FPA Detector at Room Temperature

A GaAs-based Up-Converter for Mid-Infrared Detection Utilizing Quantum Cascade Transport

A GaN/AlN Quantum Cascade Detector with a Broad Response from the Mid-Infrared (4.1 Μ M) to the Visible (550 Nm) Spectral Range

Optical Properties of Zn0.46Cd0.54Se/Zn0.24Cd0.25Mg0.51Se Multiple Quantum Wells for Infrared Photodetector Applications

Enhanced response over wavelength range of 7-12 µm for quantum wells in asymmetric micro-pillars

High-Performance Very Long Wave Infrared Quantum Cascade Detector Grown by MOCVD

A Voltage-Controlled Tunable Two-Color Infrared Photodetector Using Gaas/Alas/Gaalas and Gaas/Gaalas Stacked Multiquantum Wells