Effect of Rapid Heating and Quenching on Microstructure and Mechanical Properties of High Strength Low Alloy Steel
Kangfeng Zhu,Xinwei Wang,Zhenqiang Wang,Shuai Tong,Xiaokai Liang,Xinjun Sun,Caifu Yang
DOI: https://doi.org/10.1007/s11665-024-10429-2
IF: 2.3
2024-11-20
Journal of Materials Engineering and Performance
Abstract:In order to improve strength and toughness, a useful technique for refining grain size is the application of high heating rates during the austenitizing process. The present study investigated and analyzed the impact of conventional heating quenching and quenching at varying heating rates on the mechanical properties, microstructure, prior austenite grain size, and second phase of low alloy high strength steels. The results indicate that the prior austenite grain size was refined from 8.1 to 4.8 μm upon increasing the heating rate to 50 °C/s. Even after heating quickly to increase the holding time to 30 min, the grain size remained significantly smaller than with traditional heating. When compared to a brief time, the heating rate induced grain refining was predominant. The primary microstructure under varying heating rates was lath martensite, with carbides mostly found in the matrix as needle-shaped particles. The strength gradually rose when the heating rate was raised, and the impact energy at − 40 °C grew dramatically, with a mean value increase from 57 to 103 J. The fracture was a typical ductile fracture.
materials science, multidisciplinary