Highly Isolated Cobalt Sulfide Nanoparticles Encapsulated in 3D Hollow Nitrogen Doped Carbon Sheells for Superior Lithium and Sodium Storage
Wei Huang,Huihui Shangguan,Christian Engelbrekt,Xiaowen Zheng,Fei Shen,Xinxin Xiao,Lijie Ci,Pengchao Si,Jingdong Zhang
DOI: https://doi.org/10.1149/ma2019-04/6/356
2019-01-01
Abstract:Highly Isolated Cobalt Sulfide Nanoparticles Encapsulated in 3D Hollow Nitrogen Doped Carbon Sheells for Superior Lithium and Sodium Storage Wei Huang, a, b Huihui Shangguan, b Christian Engelbrekt, a Xiaowen Zheng, b Fei Shen, a Xinxin Xiao, a Lijie Ci, b Pengchao Si b, * and Jingdong Zhang a, * a Department of Chemistry, Technical University of Denmark, DK-2800 Kongens Lyngby, Denmark. b SDU & Rice Joint Center for Carbon Nanomaterials, Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, School of Materials Science and Engineering, Shandong University, Jinan 250061, P. R. China. Hollow materials derived from metal-organic frameworks (MOFs) present a class of promising electrode materials for energy storage technology. Herein, we report the design and nanoengineering of highly isolated cobalt sulfide nanoparticles embedded in hollow nitrogen-doped carbon shells (Co9S8/HNCS) for superior lithium and sodium storage. Initially, hollow intermediates with preserved cobalt component were prepared by simultaneously dissociating cobalt containing zeolitic-imidazolate-frameworks-67 (ZIF-67), and polymerizing dopamine in a Tris-HCl solution (pH = 8.5). The poly-dopamine (PDA) wrapped intermediates inherited the polyhedron structure of the ZIF-67 crystals. The final Co9S8/HNCS composite was obtained via a combined carbonization and sulfurization treatment of the intermediates, allowing the formation of hollow polyhedrons of nitrogen-doped carbon layers (900 ± 100 nm) derived from PDA and the encapsulation of highly monodispersed cobalt sulfide nanoparticles (11 ± 2 nm). This configuration not only shortened the ionic diffusion distance, and accommodated volume expansion during lithium or sodium ion insertion/extraction, but also promoted the overall electronic conductivity, and provided more active sites during cycling. As a result, Co9S8/HNCS composite exhibited an impressive reversible capacity of 755 mA h g-1 at 500 mA g-1 after 200 cycles for lithium ion storage, and capacities of 327 mA h g-1 at 500 mA g-1 after 200 cycles and 224 mA h g-1 at 1000 mA g-1 after 300 cycles for sodium ion storage. Essential factors associated with the structural stability and changes during cycling have been identified and the discharge/charge mechanism has been discussed. Figure 1