Controlling Transformation of Sorbitol into 1-Hexanol over Ru-MoO x /Mo 2 C Catalyst via Aqueous-Phase Hydrodeoxygenation
Xin Chen,Yanni Zheng,Qian Zhang,Songbai Qiu,Qingwei Meng,Xiaoping Wu,Tiejun Wang
DOI: https://doi.org/10.1021/acssuschemeng.1c02014
2021-06-28
Abstract:Higher alcohols are important monohydric alcohols category of synthetic chemicals and fuels. Currently, research efforts in this catalytic synthesis have been devoted to providing desirable selectivity to specific higher alcohols. In this work, for the first time, the aqueous-phase hydrodeoxygenation of sorbitol derived from biomass was proposed to efficiently synthesize renewable 1-hexanol over a multifunctional Ru-MoO<i><sub>x</sub></i>/Mo<sub>2</sub>C catalyst in a continuous-flow tubular reactor. Compared with molybdenum nitride, phosphide, sulfide, and oxide catalysts, molybdenum carbide displayed promising catalytic performance in the selective transformation of sorbitol into 1-hexanol, representing the feasibility of selectively controlling the C–O bond cleavage and preserving the original carbon chain. Studies in catalyst characterization revealed that the synergism of Ru and Mo<sub>2</sub>C was the key to manipulate the main product selectivity between 1-hexanol and 1-hexane, while the 1-hexanol selectivity was concurrently promoted by the presence of MoO<sub>x</sub>. The highest yield (28.7%) of 1-hexanol was achieved at 523 K under 6.0 MPa of hydrogen pressure. The present catalyst system was equally applicable to the selective hydrogenolysis of other sugar polyols such as xylitol, erythritol, glycerin, and ethylene glycol into the corresponding 1-pentanol, 1-butanol, 1-propanol, and ethanol. Thus, this catalytic strategy creates new opportunities for producing high value-added higher alcohols from sugar polyols over molybdenum carbide materials.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.1c02014?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.1c02014</a>.Catalyst preparation details, additional catalyst characterization data, sample liquid chromatography results; additional experimental results; schematic illustration of the preparation process for the 2Ru-2MoO<i><sub>x</sub></i>/Mo<sub>2</sub>C catalyst; experimental setup of internally interconnected fixed-bed reactor system; image of the continuous-flow fixed-bed reactor and photograph of the typical higher alcohol products with spontaneous phase-separation; XRD patterns of various Mo-based catalysts before reduction; TEM images and corresponding elemental mapping images of 2Ru-2MoO<i><sub>x</sub></i>/Mo<sub>2</sub>C; TEM and HRTEM images of Mo<sub>2</sub>C sample; typical gas chromatograms of hydrogenolysis products; XPS spectra of Mo 3d after 24 h and 132 j reaction and Ru 3p along with XRD patterns of different 2Ru-2MoO<i><sub>x</sub></i>/Mo<sub>2</sub>C samples; N<sub>2</sub> adsorption–desorption isotherms and pore size distributions of the related catalysts; XPS date of Mo 3d for different Mo<sub>2</sub>C samples before reduction; surface composition and atomic ratios of C/O determined via XPS on different Mo2C samples before reduction; acidity of various Mo<sub>2</sub>C catalysts after reduction at 623 K; Mo leaching of 2Ru-2MoO<i><sub>x</sub></i>/Mo<sub>2</sub>C catalyst in the sorbitol hydrogenolysis during long-running; textural properties of the 2Ru-2MoO<i><sub>x</sub></i>/Mo<sub>2</sub>C samples; and XPS date of Mo 3d for 2Ru-2MoO<sub>x</sub>/Mo<sub>2</sub>C samples (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.1c02014/suppl_file/sc1c02014_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology