Fast Li Ion Dynamics in Defect-Rich Nanocrystalline Li 4 PS 4 I─The Effect of Disorder on Activation Energies and Attempt Frequencies

Anna Jodlbauer,Jonas Spychala,Katharina Hogrefe,Bernhard Gadermaier,H. Martin R. Wilkening

DOI: https://doi.org/10.1021/acs.chemmater.3c02988

IF: 10.508

2024-01-17

Chemistry of Materials

Abstract:Solid-state electrolytes with fast ionic transport properties will play a crucial role in future energy storage applications that rely on electrochemical reactions. The group of lithium thiophosphates appears to be especially promising as it includes compounds such as Li10GeP2S12, already exceeding the conductivity of conventional liquid electrolytes. Recently, the I-containing thiophosphate, Li4PS4I, belonging also to this group attracted great interest due to its theoretically high ionic conductivity that is assumed from the favorable 3D percolation pathways. However, earlier studies showed that ionic conductivity is lower than expected from these structural considerations. Here, we reinvestigated both long-range and short-range ion dynamics through nuclear magnetic resonance (NMR) measurements as well as by conductivity spectroscopy to gain more insights into the conduction mechanism. It turned out that by changing the morphology of Li4PS4I, that is, by going from the coarse-grained to the nanocrystalline form, a significant increase in ion dynamics is seen that is accompanied by a change in the Arrhenius prefactor and a clear decrease in activation energy [0.35 eV (nano) and 0.49 eV (micro)] for ionic conduction. We assume that the smaller energy barrier for the nanostructured sample, which was prepared by ball milling, originates form the increased number of defects introduced through mechanical treatment. In line with the reduction in activation energy, we clearly observed an increase in room-temperature conductivity from 2.9 × 10–2 mS cm–1 (micro) to 0.47 mS cm–1 (nano), that is, by almost two orders of magnitude. Diffusion-induced spin–lattice relaxation 7Li NMR measurements reveal two distinct Li ion diffusion processes. While the slower process shows similar activation energies for both micro- and nanocrystalline Li4PS4I, the faster relaxation process displays, however, activation energies of 0.32 and 0.13 eV for the microcrystalline and the nanocrystalline sample, respectively. Additional spin-lock NMR measurements sense long-range ion transport (0.34–0.36 eV) and point to anisotropic ion conduction for both samples. Taken together, the combination of nuclear and non-nuclear methods operating on different time scales help characterize the relevant diffusion pathways in Li4PS4I finally leading to the superior behavior of nano-Li4PS4I in terms of through-going ionic conduction.

materials science, multidisciplinary,chemistry, physical

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: how to significantly improve the ionic conductivity of Li4PS4I material by changing its morphology (from coarse - grained to nanocrystalline), and explore the mechanism behind this change. Specifically, the researchers re - investigated the long - range and short - range ionic dynamic characteristics of Li4PS4I through nuclear magnetic resonance (NMR) measurement and conductivity spectroscopy methods to gain a deeper understanding of the conduction mechanism.

### Background and Problem
Solid - state electrolytes have received extensive attention because of their importance in future energy storage applications, especially in applications relying on electrochemical reactions. Lithium thiophosphate compounds, such as Li10GeP2S12, are considered particularly promising materials due to their high conductivity. However, although the thiophosphate containing iodine, Li4PS4I, has a high ionic conductivity in theory, earlier studies showed that its actual ionic conductivity was lower than expected. This has aroused the interest of researchers, hoping to reveal the reasons through further research and find ways to improve its performance.

### Research Objectives
1. **Improve Ionic Conductivity**: Observe the change in the ionic conductivity of Li4PS4I by changing it from a coarse - grained morphology to a nanocrystalline morphology.
2. **Explore the Mechanism**: Through various experimental methods (such as NMR measurement and conductivity spectroscopy), study the ionic dynamic characteristics in detail, especially the long - range and short - range ionic movements, in order to understand the mechanism of the improvement in ionic conductivity.

### Main Findings
1. **Significant Improvement in Conductivity**: The ionic conductivity at room temperature of nanocrystalline Li4PS4I prepared by mechanical ball milling method increased from 2.9×10^−2 mS cm^−1 (microcrystalline) to 0.47 mS cm^−1 (nanocrystalline), which is an increase of nearly two orders of magnitude.
2. **Reduction in Activation Energy**: The activation energy of nanocrystalline Li4PS4I decreased from 0.49 eV (microcrystalline) to 0.35 eV (nanocrystalline), indicating that the ionic migration barrier is lower in the nanocrystalline morphology.
3. **Change in Ionic Dynamics**: NMR measurements showed that there are two different lithium - ion diffusion processes in nanocrystalline Li4PS4I, and the activation energy of the faster diffusion process in the nanocrystalline sample decreased significantly (from 0.32 eV to 0.13 eV).
4. **Anisotropic Conduction**: The research shows that the ionic conduction in nanocrystalline Li4PS4I is anisotropic, which may be due to the influence of internal defects and interface effects in the material.

### Conclusion
By changing Li4PS4I from a coarse - grained morphology to a nanocrystalline morphology, its ionic conductivity can be significantly improved. This improvement is mainly attributed to the reduction in the ionic migration barrier and the change in ionic dynamics in the nanocrystalline morphology. These findings provide an important theoretical and experimental basis for further optimizing solid - state electrolyte materials.